- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 88.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 88.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648-56 |
| Rotuba 870 Ethyl Cellulose Data provided by the manufacturer. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CU6800 PC+ABS (Asia Pacific) Non-chlorinated and non-brominated flame retardant PC/ABS featuring excellent flow properties. UL-94 V1 listed at 2.0mm intended for a wide range of different applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CH020-02 Polypropylene, Thermoforming, Sheet, Film COPYLENE™ CH020-02 is a polypropylene homopolymer resin suitable for thermoforming, sheet and film fiber applications. Applications: Opaque Containers. Equivalent to Pro-fax® HL783HInformation pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | |
| Eastman Tenite 105-28 Cellulose Acetate
(discontinued **) 28% Plasticized ISO data as provided by the manufacturer, Eastman Chemical. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| LyondellBasell Pro-fax 7823 Polypropylene Impact Copolymer, Fractional Melt Flow Key Features: high extrudate melt strength, good cold impact resistance, good stiffness and impact balance, FDA acceptableApplications: pipe, tubing, sheet, profiles, netting, blown containers and i.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Flint Hills AP6106-HS Impact Copolymer Polypropylene High impact copolymer, UL certified, and FDA compliant. Features: Heat stabilizedApplications: Injection molding: child protection systems, appliance components, consumer durables, and automotive in.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical HIPS 501S PS, Impact Modified Description: Injection Molding, PS, General Purpose, Impact ModifiedApplication: Refrigerator Food Holder, Food Container, Plastic Toy, Sheet or Film of Yot ReceptacleCAS: 9003-55-8Information provi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Ineos N00GX11 Polypropylene Impact Copolymer Grade N00Gx11 is a fractional melt flow rate experimental impact copolymer for blow molding, pipe, tubing, and sheet extrusion. It offers a good balance of stiffness and impact strength as compared .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 4-8000 Polypropylene Random Copolymer INNOPOL® CS 4-8000 is a polypropylene random copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 4-8000 is highly suitable for pressure pipe manufacturing, includi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON DD0001 PC LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON MD000AP PP LNP* STAT-KON* MD000AP is a compound based on Polypropylene containing Carbon Powder. Added features of this grade include: Electrically Conductive, Exceptional Processing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Unannealed; ASTM D648 |
| Lubrizol Isoplast® 2531 Engineering Thermoplastic Polyurethane Resin for Medical Applications Features: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Unannealed; ASTM D648 |
| Lubrizol Isoplast® 301 Engineering Thermoplastic Polyurethane Resin Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ISO 75-2 |
| Borealis HB306MO Polypropylene HB306MO is a low melt-flow-rate polypropylene homopolymer intended for compression molding of caps and closures. This grade is designed for the caps and closures market and therefore contains a lubr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Annealed; ISO 75-2A |
| Total PSC 1340 Crystal Polystyrene 1340 is a high molecular weight crystal polystyrene which allows maximum dilution rates with high impact polystyrene grades such as LACQRENE® 7240. In dilution, LACQRENE® 1340 gives excellent pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3045 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Eastman Tenite Propionate 380A4000010 Clear, Trsp Cellulose Acetate Propionate Plasticizer 10%. Weight loss on heating = 0.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® ST7301 BK356 Nylon 6
(Unverified Data**) Super Toughened Polyamide 6 Zytel ST7301 BK356 is a Super Tough heat stabilized lubricated black polyamide 6 resin for injection molding and extrusion. It offers outstanding impact resistance over a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D-648 |
| Bapolan® 6450 Polystyrene Injection Molding Resin Bapolan 6450 is a high impact polystyrene resin designed for injection molding applications requiring fast cycle times, superior impact and gloss. It complies with US FDA21 CFR177.1640 and 94HB UL .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Bapolene® PP5083 Polypropylene, Injection Grade Bapolene PP 5083 is a clarified PP Random Copolymer for injection molding. This resin exhibits good processing and impact properties. This product meets FDA regulation 21CFR 177.1520 and is suitab.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Carmel Olefins CAPILENE® Y 50 V Polypropylene Homopolymer CAPILENE® Y 50 V is an ultra high melt flow rate polypropylene homopolymer suitable for thin walled injection molding and as a base resin for compounds applications. The product combines high stiff.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Lubricomp CI001 PS (Asia Pacific) LNP* Lubricomp* CI001 is a compound based on Polystyrene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pa.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL FN215X PPE+PS Structural foam resin. 170F (77C) HDT. Improved reliability and productivity. All values at 20% weight reduction. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL PX1005X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. UL746C F1. Excelent dielectric strength. Suitable for E/E market in indoor/outdoor applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PX1005X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. UL746C F1. Excelent dielectric strength. Suitable for E/E market in indoor/outdoor applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Eastman Tenite Propionate 350E0096914 Natural, Trsp Cellulose Acetate Propionate Plasticizer 12%. Weight loss on heating = 0.5% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| BP Amoco Acclear® 8649X Random Copolymer Polypropylene, High Clarity Grade
(discontinued **) Developmental Grade. Suggested fabrication methods: Injection molding; Stretch blow moldingFeatures: Ultra high clarity, Low taste/odor, Excellent processabilityTypical applications: High clarity c.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Buckeye Polymers BP RPP 4012 C Polypropylene, 40% Mineral Filled Calcium carbonate-filled PP grades have a high impact toughness, moderate increased stiffness, and excel in high gloss applications. This material can be customized through the addition of UV packag.. |
|||