- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 86.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 86.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® FR15U ABS Flame retardant ABS with excellent indoor UV properties and excellent processing. UL94 V-0/5VA rated. Elevated UL RTI rating (90-85-90) for all colors except for blue and green colors (60-60-60). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® FR15U ABS (Asia Pacific) Flame retardant ABS. Excellent indoor UV properties. Excellent moldability. UL94 V-0/5VA rated.ing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® INP222 ABS Bulk MMASAN. Provides an economical option for achieving greater melt strength in polymers. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Geloy XTWM200 ASA ASA resin for injection molding. Excellent flow, colorability and outdoor weathering capability.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CR027 Polypropylene, Homopolymer, Mini-random, BOPP Mini-random homopolymer. Applications: BOPP film. Equivalent to Pro-fax® HL456JInformation provided by Phillips 66. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 - 202 °C | 187 - 396 °F | Average value: 122 °C Grade Count:14 |
| Overview of materials for ABS/Polyester Alloy This property data is a summary of similar materials in the MatWeb database for the category "ABS/Polyester Alloy". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CH085 Polypropylene, Homopolymer, Cast Film COPYLENE™ CH085, a controlled rheology polypropylene homopolymer resin, is used in injection molding and cast film extrusion applications. Applications: Bags & Pouches, Stationery Film, Stretch Wra.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CH085S Polypropylene, Homopolymer, Cast Film, Slip COPYLENE™ CH085S is a controlled rheology polypropylene homopolymer resin containing slip additive. COPYLENE™ CH085S is used in injection molding and cast film extrusion applications. Applications.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | |
| Eastman Tenite 105-33 Cellulose Acetate
(discontinued **) 33% Plasticized ISO data as provided by the manufacturer, Eastman Chemical. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | |
| LyondellBasell Lupolen® 6031 M HDPE, Injection Molding Grade Easy flow, injection molding grade for fruit crates, tote boxes and bottle crates, cartridges, protective headgear, buckets, dishes, cartridges for adhesive film canisters, aerosol lids, child seats.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Flint Hills 13T25A Random Copolymer Polypropylene Features: Excellent clarity, blush resistant and good flexural modulus. Product does not contain animal derived components.Applications: Injection Molded - Lab ware, food packaging and medical. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Flint Hills P9H8M-015 Polypropylene Specialty polypropylene, UL certified, and FDA compliant.Applications: Extrusion coating.Former Huntsman polypropylene products are now produced by Flint Hills Resources. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-loy A3000Z ABS LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY AX11421 ABS LNP* STAT-LOY* AX11421 is a compound based on ABS resin. Added feature of this material is: Antistatic. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Thermocomp CF006 PS (Europe-Africa-Middle East) LNP* Thermocomp* CF006 is a compound based on Polystyrene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® EA-0640 ABS, Unreinforced Permanent static prevention ABS material such as LCD carrierInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Samyang Triel® 5501BM Thermoplastics Polyetherester Elastomer, Blow Molding Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5501BM is for blow molding applications.Applications: Automotive BellowsInformation provided by Samyang... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ISO 75-2 |
| Borealis HB600TF Polypropylene HB600TF is a low melt flow rate polypropylene homopolymer intended for extrusion and thermoforming. Its very good organoleptic properties allows this grade to be used with any master batch without .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Formosa Plastics Formolene® 6600A Impact Copolymer Polypropylene Impact Copolymer for Extrusion and Compounding Applications (Fractional Melt Flow) Formolene® 6600A is a high impact copolymer with an excellent balance of toughness and stiffness. It is suitable f.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Total PPC 5724 Polypropylene, Extra High Impact Copolymer ATOFINA 5724 is characterized by a high fluidity offering a combination of processing and excellent impact properties in applications ranging from industrial to household.ApplicationATOFINA 5724 has.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ISO 75-2 |
| Borealis RB206MO Polypropylene Random Copolymer RB206MO is a random copolymer with good transparency and contact clarity, very good gloss and surface finish. The high stiffness of this grade allows for a reduction in cycle time. This grade also .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Eastman Tenite 350A4861313 Cellulose Acetate Propionate, Clear, Trsp Applications:Blood TherapyDrug DeliveryIV ComponentsMedical DevicesSurgical InstrumentsProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughne.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ASTM-D648 |
| Braskem RP 344 RACO Random Polypropylene Copolymer RP 344 is a medium melt flow rate random copolymer. It is suitable for blown and cast film extrusion and features good processability, excellent optical properties, and outstanding sealability. Its .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ASTM D-648 |
| Bapolan® 6055 Polystyrene, Injection Molding Bapolan PS6055 is a crystal polystyrene resin designed for injection molding applications requiring fast cycle times and superior optical properties. It complies with US FDA21 CFR177.1640 and 94HB .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | |
| BASF Polystyrol® 445 E WU Impact Grade Polystyrene (Europe) Easy flowing, heat-resistant, medium-impact, flame-retardant grade. Application example: electrical distribution boxes.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | |
| Eastman Eastalloy DA107 PC+PET Copolyester/Polycarbonate
(discontinued **) ISO data as provided by the manufacturer, Eastman Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ISO 75 |
| Polyram RamShine PV504WT/GR Acrylonitrile Butadiene Styrene, Flame Retardant Flame retardant, UV stabilized ABS for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 - 228 °C | 187 - 442 °F | Average value: 200 °C Grade Count:24 |
| Overview of materials for Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified". Each property range of values reported.. |
|||