SABIC Innovative Plastics LNP STAT-LOY AX11421 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY AX11421 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-LOY* AX11421 is a compound based on ABS resin. Added feature of this material is: Antistatic.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Moisture Absorption | 2.00 % | 2.00 % | 50% RH, 24 hrs; ASTM D570 |
| 3.70 % | 3.70 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D638 |
| 21.0 MPa | 3050 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | Type I, 5 mm/min; ASTM D638 |
| 30.0 MPa | 4350 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 48 % | 48 % | Type I, 5 mm/min; ASTM D638 |
| 81 % | 81 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.4 % | 4.4 % | 5 mm/min; ISO 527 |
| 4.7 % | 4.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.31 GPa | 190 ksi | 1 mm/min; ISO 527 |
| 1.41 GPa | 205 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| Flexural Yield Strength | 44.0 MPa | 6380 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.33 GPa | 193 ksi | 2 mm/min; ISO 178 |
| 1.35 GPa | 196 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 4.25 J/cm | 7.96 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 29.0 J @Temperature 23.0 °C |
21.4 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 20.0 J | 14.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 113 µm/m-°C @Temperature -30.0 - 30.0 °C |
62.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 126 µm/m-°C @Temperature -30.0 - 30.0 °C |
70.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 69.0 °C @Thickness 3.20 mm |
156 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+7 - 1.00e+9 ohm | 1.00e+7 - 1.00e+9 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Molding M5005 Polyvinyl Chloride, Rigid (PVC, Rigid)
- PolyOne Dynaflex™ G2701-1000-02 Thermoplastic Elastomer (TPE)
- Lord Adhesives Thermosetâ„¢ SC-102 Unfilled Silicone Encapsulant
- LG Chemical LUPOY EF1006F PC, Halogen Free, Flame Retardant, High Heat Resistance
- SABIC Innovative Plastics LNP STAT-KON DX05474 PC (Asia Pacific)
- Total PS CPDS 827 Flame Retardant Polystyrene
- Asahi Kasei Tenac® FS410 Homopolymer Acetal Resin
- CENTROPLAST CENTROLYTE ZX Polyethylene terephthalate with lubricant
- 3M 5153 PTFE Glass Cloth Tape
Copyright © lookpolymers.com All Rights Reserved