Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
NYCOA 1417 HS Heat Stabilized, Impact Modified Nylon 6 Resin NYCOA 1417 HS is a heat stabilized and impact modified Nylon 6. This medium viscosity resin was developed for injection molding and extrusion processes for applications requiring improved toughness,.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
Nylene® 603 Nylon 6, Extrusion Grade Dry as molded. Extrusion grade. Nylene 603 is a plasticized, high residual monomer resin designed for extrusion applications requiring excellent flexibility, high strength and good abrasion resist.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
Ravago Manufacturing Americas Hylon® N2000STHL Nylon 6 (DAM) Information provided by Ravago. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
Ravago Manufacturing Americas Hylon® N2000THL Nylon 6 (DAM) Information provided by Ravago. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | ASTM D648 |
Polymer Resources NY6-IM1-[color]H Nylon, Impact Modified, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
LATI LATAN 13 K/30 30% Carbon Fiber Reinforced Polyoxymethylene Copolymer (POM)
(Unverified Data**) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
PolyOne Stat-Tech™ NJ-10SS/000 Nylon 12 - 10% Stainless Steel Reinforced
(discontinued **) Data provided by PolyOne. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Unannealed |
Aardvark Polymers AARTEL® 2100UV Acetal Homopolymer Rotational Molding Resin Aartel 2100UV is a natural acetal homopolymer with UV stabilizers.Aartel 2100UV is a medium viscosity resin with excellent flow characteristics.Aartel 2100UV is available in natural white and may be.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C @Thickness 3.20 mm |
334 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics LNP Lubricomp RP0049 PA 66 LNP LUBRICOMP* RP0049 is a compound based on Nylon 66 resin containing Flame Retardant, PTFE, Silicone. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP f.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® POM HO UV Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: HomopolymerInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
Techmer ES Luriblend® POM CO GF10 TL10 BK 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightAdditive: PTFE Lubricant(10%)Features: Lubricated, Copolymer, Good Wear Resistance and Low FrictionApp.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
Techmer ES Luriblend® POM CO GF10 TX15 BK 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightAdditive: PTFE Lubricant(15%)Features: Lubricated, Copolymer, Good Wear Resistance and Low FrictionApp.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
Techmer ES Plastiblend® PA6/6,6 IM HS L Nylon 6/66 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Copolymer, Impact Modified and LubricatedProcessing Method: Injection Mold.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Asia Pacific) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Europe-Africa-Middle East) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics NORYL PPX ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
Cheng Yu Plastic T881 Flame Retardant PBT |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
Ensinger DELRIN® 100AF Acetal Homopolymer, 13% PTFE filled (POM) Ensinger’s DELRIN®100AF blend stock shapes are a 13% PTFE fiber filled homopolymer acetal. They offer an improved coefficient of friction, better lubricity, and improved wear characteristics over .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
Ensinger DELRIN® AF DE588 Acetal Homopolymer, 20% PTFE filled (POM) DELRIN® AF DE588 is a 20% PTFE filled homopolymer acetal that is fully tested and certified for use by the United States Navy. The resin is manufactured by DuPont and is used extensively in a varie.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
Ensinger Tecaform™ HPV 13 Acetal Homopolymer - Extruded Products (POM) Tecaform™ HPV 13 is a brown homopolymer acetal with an internal PTFE lubricant. Its low coefficient of friction, excellent PV values, toughness, wear resistance, and machinability make it an excep.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM Test |
BASF Ultramid® 8253 PA6 (Dry) Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/o.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | |
Arkema Group Rilsan® BESN G9 TL Nylon 11, Graphite Filled (Conditioned) Designation ISO 1874-PA11,EHLS,18-010,CD10Grade with graphite filler for tubes extrusion. Available color: steel gray. Light and heat stabilized.No need of lubricant. Low friction coefficient. Good .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
Ashley Polymers Ashlene® RH190ST Acetal A high impact homopolymer resin.Data provided by the manufacturer |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
A. Schulman ComAlloy Hiloy® 125 Polypropylene, Glass Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.50% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM Data |
BASF Capron® 8253 Impact Modified Nylon 6 (Dry)
(discontinued **) Capron 8253 is an unfilled type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Capron 8253 HS) and/or pigmented versions.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
Beijing Ranger Chem PBT-201-G0 211 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |