Polymer Property : CTE, linear, Transverse to Flow = 62.0 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| SABIC Innovative Plastics Lexan® 923X PC (Asia Pacific) Lexan*923x is a UV stabilized high flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low temperatur.. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
34.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP LUBRICOMP DFP34 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFP34 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Silicone. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| SABIC Innovative Plastics Lexan® 923X PC Lexan*923x is a UV stabilized high flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low temperatur.. |
|||
| CTE, linear, Transverse to Flow | 62.0 - 95.0 µm/m-°C | 34.4 - 52.8 µin/in-°F | Average value: 74.6 µm/m-°C Grade Count:25 |
| Overview of materials for Polycarbonate/ASA Alloy, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ASA Alloy, Unreinforced". Each property range of values reported is minimum and maximum va.. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
34.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP COLORCOMP G1000 PSU (Europe-Africa-Middle East) LNP* COLORCOMP* G1000-GY4A805-0 is a compound based on Polysulfone resin. Added features include: Custom Color Grey. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
34.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL12 PC LNP* Lubricomp* DFL12 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature 20.0 °C |
34.4 µin/in-°F @Temperature 68.0 °F |
|
| Cookson Group Plaskon® 1031 Conventional Encapsulant
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A low cost, conventional molding compound recommended for high volume commodity-type packages that house simple linear and discre.. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature 20.0 °C |
34.4 µin/in-°F @Temperature 68.0 °F |
|
| Cookson Group Plaskon® 3400 Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A reduced-stress epoxy molding compound for the encapsulation of a variety of semiconductor devices ranging from small lead count.. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
34.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP LUBRICOMP RFN1ASXS PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFN1ASXS is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
34.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP STAT-KON DFD02EXC PC (Europe-Africa-Middle East) LNP* Stat-kon* DFD02EXC is a compound based on Polycarbonate resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
34.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP STAT-LOY AX06484 ABS LNP* STAT-LOY* AX06484 is a compound based on ABS resin containing Talc. Added feature of this grade is: Antistatic, Extrudeable. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
34.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| SABIC Innovative Plastics LNP Stat-loy AX06484X ABS LNP* Stat-Loy* AX06484 is a compound based on ABS resin containing mineral filler. Characteristics of this grade is it is extrudeable and static dissipative.This data was supplied by SABIC-IP for t.. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
34.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP THERMOCOMP DF0079 PC (Europe-Africa-Middle East) LNP* Thermocomp* DF0079 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
34.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP THERMOCOMP RF008 PA 66 LNP* THERMOCOMP* RF-1008 is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
34.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP THERMOCOMP ZFM3314 PPE (Europe-Africa-Middle East) glas, mineral filled PPE |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
34.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP THERMOCOMP RF008XXH PA 66 LNP* THERMOCOMP* RF008XXH is a compound based on Nylon 66 resin containing 40% Glass Fiber. Added feature of this material includes: Healthcare. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C | 34.4 µin/in-°F | ISO 11359-1/-2 |
| Covestro Bayblend® T88 GF-10* Polycarbonate + SAN Glass Filled Impact Grade Developmental productInjection molding grade10 % GFoptimized heat ageing- and UV-stabilityvery good flowtensile modulus = 5100 MPaVicat/B 120 = 134 °CPreprocessingMax. Water content |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C | 34.4 µin/in-°F | DAM; ISO 11359-1/-2 |
| DuPont Performance Polymers Minlon® 22C BK086 Nylon 66
(Unverified Data**) 38% Mineral/Glass Reinforced Polyamide 66 Minlon 22C BK086 is a 38% mineral/glass reinforced heat stabilized black polyamide 66 resin for injection molding.Information provided by DuPont Performance.. |
|||
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C | 34.4 µin/in-°F | DAM; ISO 11359-1/-2 |
| DuPont Performance Polymers Zytel® HTN FR52G30NHF BK337 Polyphthalamide (PPA) 30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide with Improved Flow Zytel HTNFR52G30NHF BK337 is a 30% glass reinforced flame retardant lubricated high performance.. |
|||