SABIC Innovative Plastics LNP THERMOCOMP ZFM3314 PPE (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP ZFM3314 PPE (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
glas, mineral filled PPE
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Melt Index of Compound | 17 g/10 min @Load 5.00 kg, Temperature 300 °C |
17 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.10 GPa | 885 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
17.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
34.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 179 °C | 354 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Nye Lubricants 368AX-1 (RL) Synthetic Oil
- DuPont™ Surlyn® 8527 Ionomer Resin, Sodium (discontinued **)
- Lushan PF-3 Adhesive Resin for Coextruded Multi-layer Barrier Packaging Film
- Struktol TR EBS Processing Additive, Dispersant
- Borealis MG9647B Polyethylene
- A. Schulman POLYBATCH™ Weatherwood 60190U Concentrate Based In LLDPE
- Hexcel® Redux® 206-NA Foaming adhesive film
- Chosun Refractories SAL95 Special High Alumina brick
- C.O.I.M. LARIPUR® LPR2102-85AE Polycaprolactone Ester Polyurethane
Copyright © lookpolymers.com All Rights Reserved