- Polymer Property : Vicat Softening Point = 174 °F
Polymer Property : Vicat Softening Point = 174 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 79.0 °C | 174 °F | Rate B/50; ISO 306 |
| SABIC Innovative Plastics Geloy XTWE480 ASA (Asia Pacific) Anti-scratch Geloy grade with excellent weatherability, high flow, and good surface quality. XTWE480 is available in various colours.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Vicat Softening Point | 79.0 - 182 °C | 174 - 360 °F | Average value: 136 °C Grade Count:6 |
| Overview of materials for Thermoplastic Polyurethane, Elastomer, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane, Elastomer, Glass Filled". Each property range of values reported is minimum .. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | 1kg load; ASTM D1525 |
| Eastman 7352 PET
(discontinued **) VORIDIAN PET thermoplastic polyesters are condensation polymers produced by a continuous melt-phase polymerization process followed by a solid-state polymerization process. VORIDIAN PET polyester 73.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| DuPont Bynel® 3030 Anhydride-Modified Ethylene Vinyl Acetate Adhesive Resin
(discontinued **) Bynel® Series 3000 resins are anhydride-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process p.. |
|||
| Vicat Softening Point | 79.0 - 81.0 °C @Load 5.00 kg |
174 - 178 °F @Load 11.0 lb |
ISO R306 |
| Fainplast Compounds RE 337 Rigid PVC, Extrusion Cheap profiles |
|||
| Vicat Softening Point | 79.0 - 81.0 °C @Load 5.00 kg |
174 - 178 °F @Load 11.0 lb |
ISO R306 |
| Fainplast Compounds RI 059/1 Rigid PVC, Injection Molding Fittings high fluidity |
|||
| Vicat Softening Point | 79.0 - 81.0 °C @Load 5.00 kg |
174 - 178 °F @Load 11.0 lb |
ISO R306 |
| Fainplast Compounds RI 54 Rigid PVC, Injection Molding Fittings for building trade - high fluidity |
|||
| Vicat Softening Point | 79.0 - 81.0 °C @Load 5.00 kg |
174 - 178 °F @Load 11.0 lb |
ISO R306 |
| Fainplast Compounds RI 55 Rigid PVC, Injection Molding Fittings for building trade - high fluidity |
|||
| Vicat Softening Point | 79.0 - 81.0 °C @Load 5.00 kg |
174 - 178 °F @Load 11.0 lb |
ISO R306 |
| Fainplast Compounds RKS 218/W Rigid PVC, Antishock Extrusion Lead Free Antishock profiles |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| DuPont Elvax® 660 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525, ISO 306 |
| DuPont Elvax® 670 Ethylene Vinyl Acetate DuPont™ Elvax® 670 is an ethylene-vinyl acetate copolymer resin for use in industrial applications.Applications:Elvax® 670 resins can be used for the following applications: molding, compounding .. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| DuPont Elvax® 670 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ISO 306 |
| Total EVA 1020 VN 3 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1020 VN 3 is made by a high pressure tubular process. Grade for flexible, very transparent films with high strength and very good sealability. Contains an antioxidant.Application examples: Thi.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | A50; DIN 53460 |
| Lubrizol ESTANE® 58092 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| DuPont Nucrel® AE High Performance Adhesive and Sealant Resin Nucrel® Nucrel® AE is a terpolymer of ethylene, methacrylic acid, and acrylate, available for use in conventional extrusion coating, coextrusion coating, and extrusion laminating equipment designe.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| Eastman Cadence™ GS4 Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | 1kg load; ASTM D1525 |
| Eastman Eastar EN052 Polyester Eastar Polyester EN052 is a thermoplastic condensation homopolymer produced by a continuous melt-phase polymerization process followed by a solid-state polymerization process. It has been crystalliz.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | 5kg load; ISO 306 |
| Eastman Eastar MN004 Copolyester Eastar Copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN004 contains a mold release.Appl.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525, ISO 306 |
| DuPont™ Nucrel® 3990L Ethylene Acrylic Acid Nucrel® 3990L is a copolymer of ethylene and acrylic acid. It is available for use in conventional extrusion coating, coextrusion coating and extrusion laminating equipment. 9.5 % By Weight Acrylic.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| DuPont™ Surlyn® 1652 Zinc Ionomer Resin for Flexible Packaging Surlyn® 1652 is an ionomer resin available for use in blown/cast film and extrusion coating operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylene .. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | |
| Dow ATTANE™ 4403 Ultra Low Density Polyethylene, Blown Film Grade ATTANE® 4403 copolymer is an ultra low density polyethylene having high impact, tear strength and exceptional flexibility. It is designed for use in industrial/consumer blown film applications and .. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| Braskem PB 608 LDPE Injection Molding Polyethylene Description: PB608 is a grade produced under high pressure in an autoclave reactor. This grade is especially designed for injection molding of articles that must show excellent flexibility propertie.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| Braskem PB608 Injection Molding Low Density Polyethylene Injected lids and caps; Large flat surface injected pieces.Information provided by Braskem. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| Arkema Group OREVAC® 9309 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | 50°C/hr; 50N |
| Arkema Group Kynar® FLEX 2801 PVDF
(discontinued **) Designation ISO 12086-VDF/HFP-K, EDN, N. ?E7.D.G.B.C,, ? (3.5-7.5)Kynar FLEX PVDF are fluorinated thermoplastic copolymers.Outstanding characteristics of Kynar FLEX: chemical resistance, imperviousn.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| DuPont™ Surlyn® 1652SB Zinc Ionomer Resin for Blown/Cast Film and Extrusion Coating Surlyn® 1652SB is an ionomer resin available for use in blown/cast film and extrusion coating operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylen.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| DuPont™ Surlyn® 1652SR Zinc Ionomer Resin for Cast Film and Extrusion Coating Surlyn® 1652SR is an ionomer resin available for use in cast film and extrusion coating operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylene resi.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | 50N (T° increase = 5°C/h); ISO 306B50 |
| Total Lacqrene® 2901 Medium Impact Polystyrene
(discontinued **) LACQRENE® 2901 is a very easy flowing, medium impact polystyrene for injection molding. The very high flow of this grade allows for the production of thin wall section or long flow path molding on.. |
|||
| Vicat Softening Point | 79.0 °C | 174 °F | temperature B; ISO 36 |
| Lubrizol ESTALOC® 59003 Ester-Type, Reinforced Engineering Thermoplastic (European Grade) Description: Estaloc® RETP (Reinforced Engineering Thermoplastic) is a tough, dimensionally stable, abrasion-resistant thermoplastic that withstands demanding environments. Developed as an extensio.. |
|||