Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 20.7 MPa @Temperature 177 °C |
3000 psi @Temperature 350 °F |
Short-Beam, Dry, Autoclave; ASTM D2344 |
Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac.. |
|||
Shear Strength | 20.7 MPa @Temperature 37.8 °C |
3000 psi @Temperature 100 °F |
ASTM D732 |
Greene Tweed Avalon® 1 PTFE Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin.. |
|||
Shear Strength | 20.7 MPa @Temperature 26.7 °C |
3000 psi @Temperature 80.0 °F |
ASTM D732 |
Greene Tweed Avalon® 7 PTFE, Pigmented and Molybdenum Filled Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin.. |
|||
Shear Strength | 20.68 MPa @Temperature 177 °C |
3000 psi @Temperature 350 °F |
90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1002 |
Zyvex Performance Materials Aroply™ 350 Nano-Engineered Composite Film Adhesive Aroply™ 350 Film Adhesive is a versatile, heat curing carbon-nanotube modified epoxy structural film adhesive available in a variety of film weights on a supported carrier. Cured adhesive character.. |
|||
Shear Strength | 20.7 MPa @Temperature 71.1 °C |
3000 psi @Temperature 160 °F |
Tensile Shear, Redux 775 film |
Hexcel® Redux® 775 Vinyl phenolic structural adhesive Redux 775 was adopted as the world's first metal-to-metal bonding process to be officially approved for use in the manufacture of aircraft primary structures in 1943. It is available either as a fil.. |
|||
Shear Strength | 20.7 MPa @Temperature 24.0 °C |
3000 psi @Temperature 75.2 °F |
Overlap |
3M Scotch-Weld™ 1838 B/A Green Two-Part Structural Adhesive Multi-purpose and Rigid bondsInformation provided by 3M |
|||
Shear Strength | 20.7 MPa @Temperature -55.0 °C |
3000 psi @Temperature -67.0 °F |
Overlap |
3M Scotch-Weld™ 2086 One-Part Epoxy Adhesives and Metal Primer High Temperature strength and High ViscosityInformation provided by 3M |
|||
Shear Strength | 20.7 MPa @Temperature -53.0 °C |
3000 psi @Temperature -63.4 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Hi-Dense Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Dense is a deareted version of Scotch-Weld adhesive 2214 regular for use where a very dense, void free bondline is required. One part 250°F (121°C) curing 100% .. |
|||
Shear Strength | 20.7 MPa @Temperature 82.0 °C |
3000 psi @Temperature 180 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Hi-Temp Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids, 3M™ Sc.. |
|||
Shear Strength | 20.7 MPa @Temperature -55.0 °C |
3000 psi @Temperature -67.0 °F |
Overlap |
3M Scotch-Weld™ EC2216 Structural Adhesive High Performance, Very flexible bondsInformation provided by 3M |
|||
Shear Strength | 20.7 MPa @Temperature 65.0 °C, Time 3600 sec |
3000 psi @Temperature 149 °F, Time 1.00 hour |
Lap, Alum to Alum |
Atom Adhesives AA-BOND F112 Epoxy Adhesive AA-BOND F112 is an impact resistant, fiber-optic adhesive. AA-BOND F112 is two-part, low viscosity epoxy has the distinct advantage of remaining below 3000 cps for a minimum of 40 minutes. AA-BOND F.. |
|||
Shear Strength | 20.7 MPa @Temperature 65.0 °C, Time 14400 sec |
3000 psi @Temperature 149 °F, Time 4.00 hour |
Lap, Alum to Alum |
Atom Adhesives AA-BOND F110 Epoxy Adhesive AA-BOND F110 is a rigid, optically clear adhesive with a very low viscosity. AA-BOND F110 is room temperature system an excellent choice for thin bond-line assembly and repair applications of prisms.. |
|||
Shear Strength | 20.7 MPa @Temperature -55.0 °C |
3000 psi @Temperature -67.0 °F |
Overlap |
3M Scotch-Weld™ 1386 One-Part Epoxy Adhesives and Metal Primer High Temperature strength and Impact resistanceInformation provided by 3M |
|||
Shear Strength | 20.7 MPa @Temperature -53.0 °C |
3000 psi @Temperature -63.4 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Regular Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Regular is an aluminum filled general purpose product for use in applications where high strength bonds are needed in a temperature range of -53-121°C.One part 250°.. |