- 3M Scotch-Weld™ EC2216 Structural Adhesive
3M Scotch-Weld™ EC2216 Structural Adhesive
| Category | Polymer , Adhesive |
| Manufacturer | 3M |
| Trade Name | Scotch-Weld™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | 3M Scotch-Weld™ EC2216 Structural Adhesive.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Performance, Very flexible bondsInformation provided by 3M
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 80000 cP | 80000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Shear Strength | 2.76 MPa @Temperature 82.0 °C |
400 psi @Temperature 180 °F |
Overlap |
| 20.7 MPa @Temperature -55.0 °C |
3000 psi @Temperature -67.0 °F |
Overlap | |
| 22.1 MPa @Temperature 24.0 °C |
3200 psi @Temperature 75.2 °F |
Overlap | |
| Peel Strength | 4.38 kN/m | 25.0 pli | T-Peel |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.5 @Frequency 1000 Hz |
3.5 @Frequency 1000 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 600 min | 10.0 hour | Time to Handling Strength |
Users viewing this material also viewed the following:
- Karina 40/418-FC-LMP Green Color Concentrate for PVC
- Karina 732-36/563-W-ERB Compound PVC Brown
- Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes
- SABIC Innovative Plastics LNP LUBRICOMP RFP36XXZ PA 66 (Asia Pacific)
- Wellman Wellamid® GSF25/15-66 22LH-N 40% Glass Sphere/Fiber Reinforced Nylon 66
- DSM Akulon® Ultraflow™ K-FHG6 Nylon 6-30% Glass Reinforced (European Grade) (Dry)
- ACC EP RAP-1567 EPI Engineered Polymers Aliphatic Polyurea
- BorsodChem ONGRONAT PA-26 MDI Isocyanate
- Azoty Tarnow™ Tarnamid® T-27 GF30 FRV2 Polyamide 6 - Flame Retarded, Reinforced
- Garlock GYLON® 3504 PTFE Gasketing, Glass Microsphere Filled
Copyright © lookpolymers.com All Rights Reserved