- Polymer Property : Flexural Modulus = 508 ksi
Polymer Property : Flexural Modulus = 508 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 3.50 GPa | 508 ksi | 1.5mm/min; ISO 178:2001 |
| Nylacast Oilon Cast Nylon 6, Lubricated (Lubricant Oil Filled) This exceptional oil-loaded nylon features a complex blended oil lubrication system, uniformly distributed throughout the product, that guarantees constant performance over the whole service life. E.. |
|||
| Flexural Modulus | 3.50 GPa @Temperature 23.0 °C |
508 ksi @Temperature 73.4 °F |
ISO 178 |
| Polykemi AB POLYblend 45FS GF20 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® EXL4019 PC Lexan* EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers im.. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 |
| PolyOne Geon™ CPVC MC250 Polyvinyl Chloride, Chlorinated (CPVC) The Geon MC250 CPVC is an injection molding fittings compound for Industrial Pipe applications where enhanced resistance at elevated temperatures is needed. It is listed under NSF Std 14 and 61. Geo.. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | |
| Lehmann & Voss LUVOCOM® 1105-8356 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | |
| Lehmann & Voss LUVOCOM® 20-0664 Polyphthalamide, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low influence from moisture an.. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | |
| Lehmann & Voss LUVOCOM® 6-8548 Polyamide 12, with glass fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Suitable for discharging of statically generated electricity.Dynamic stressed parts.Low waterab.. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | |
| Lehmann & Voss LUVOCOM® 80-8387 Polyacetal-copolymer, unreinforced Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Isotropic shrinkage characteristics.Strong, stiff parts.Impact resistance.Control disks, cams, .. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | |
| Lehmann & Voss LUVOCOM® 80-8387/EM Polyacetal-copolymer, unreinforced Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Isotropic shrinkage characteristics.Strong, stiff parts.Impact resistance.Control disks, cams, .. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 |
| Loxim 315 02HB Nylon 6 Information provided by Loxim Industries |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | Tangent; ASTM D790 |
| Fiberfil® J-68/25/E/SD Polypropylene Copolymer, 25% Glass Fiber Reinforced, Chemically coupled, with static dissipation Information provided by FIBERFIL Engineered Plastics |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP RAL22 PA 66 LNP LUBRICOMP* RAL22 is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP RBG16I PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RBG16I is a compound based on Nylon 66 resin containing Glass Bead, Graphite. Added features of this material include: High Impact. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | DIN 53457 |
| Schwartz Technical Plastics LAMIGAMID® 510 Polyethylene Terephthalate Application: friction bearings, wear linersInformation provided by Schwartz Technical Plastics GmbH |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Ultem DT1800E PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri.. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 |
| Solvay Specialty Polymers KetaSpire® KT-820 SL10 Polyetheretherketone (PEEK) KetaSpire® KT-820 SL10 is a polyetheretherketone (PEEK) based compound designed to offer enhanced lubricity and reduced friction compared to standard PEEK. Unlike other grades formulated for wear.. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® 4512 PBT+PC (Europe-Africa-Middle East) 10% GF FR PBT/PC Blend |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Xenoy® X4850 PBT+PC (Asia Pacific) Xenoy X4850 is a hydrostable, high modulus, high ductile PC/PBT blend. Furthermore, this resin provides high chemicalresistance, very low creep, low CTE, excellent fatique and high heat dimensional .. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | |
| Hexcel® HexPly® M21 356°F (180°C) Curing Epoxy Matrix HexPly® M21 is a new, very tough epoxy matrix that exhibits excellent damage tolerance, especially at high energy impact. It has been developed to meet the needs of the latest generation of primary.. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM-D790 |
| Polyram PlusTek PB847I4 Nylon 6, 20% Glass Fiber and Mineral 20% glass fiber and mineral reinforced, impact modified polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D 790 |
| Cossa Polimeri ESTACARB 0820 GF V0 HF Flame Retardant Polycarbonate Polycarbonate with 10% glass fiber reinforcementFlame retardant class V0, antimony, chlorine and bromine free, high stiffness, high dimensional stability, good processability, good light resistanceI.. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | 0.05 in/min; ISO 178 |
| CTC X-PRO TF 1140 HP Polypropylene Homopolymer, 40% Talc Filled X-PRO TF 1140 HP is a 40% talc reinforced polypropylene homopolymer, heat stabilized, and made of 98% recycled content. It has applications in: automotive under hood, IP components, HVAC, and lawn .. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 |
| E-Polymers TEKANATE™ G710 , 10% Glass Fiber Reinforced Poly Carbonate 10% Glass Fiber reinforcedInformation provided by E-Polymers Co. Ltd. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO 178 |
| Cossa Polimeri ESTABLEND PA 2516 GF ABS / Nylon 6 Blend, 8% Glass Filled ESTABLEND PA is a blend of acrylonitrile butadiene styrene and polyamide 6.8% glass fiber reinforcedExceptional chemical resistance, excellent heat resistance, good dimensional stabilityInformation .. |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 |
| Ashley Polymers Ashlene® P284 PPE Alloy, 10% Glass Reinforced A 10% glass reinforced PPE Alloy for superior properties and chemical resistance with high heat resistance.Data provided by the manufacturer |
|||
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 |
| Beijing Chemical Industry KAIFA® 201-G15R PBT Resin 20% glass fiber reinforced, good flow and toughnessInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||