Cossa Polimeri ESTABLEND PA 2516 GF ABS / Nylon 6 Blend, 8% Glass Filled

Category	Polymer , Thermoplastic , ABS Polymer , Nylon , Nylon 6
Manufacturer	Cossa Polimeri S.r.L.
Trade Name	ESTABLEND PA
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Cossa Polimeri ESTABLEND PA 2516 GF ABS / Nylon 6 Blend, 8% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

ESTABLEND PA is a blend of acrylonitrile butadiene styrene and polyamide 6.8% glass fiber reinforcedExceptional chemical resistance, excellent heat resistance, good dimensional stabilityInformation provided by Cossa Polimeri S.r.l.

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	ISO 2577
Melt Flow	27 g/10 min <br>@Load 10.0 kg,<br> Temperature 240 °C	27 g/10 min <br>@Load 22.0 lb,<br> Temperature 464 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	ISO 527
Elongation at Break	3.0 %	3.0 %	ISO 527
Tensile Modulus	3.70 GPa	537 ksi	ISO 527
Flexural Modulus	3.50 GPa	508 ksi	ISO 178
Izod Impact, Notched	0.0600 J/cm <br>@Temperature 23.0 °C	0.112 ft-lb/in <br>@Temperature 73.4 °F	ISO 180/A

Thermal Properties	Metric	English	Comments
Vicat Softening Point	115 °C <br>@Load 5.00 kg	239 °F <br>@Load 11.0 lb	50°C/hr; ISO 306
	190 °C <br>@Load 0.999 kg	374 °F <br>@Load 2.20 lb	50°C/hr; ISO 306
Flammability, UL94	HB <br>@Thickness 1.60 mm	HB <br>@Thickness 0.0630 in
	HB <br>@Thickness 3.20 mm	HB <br>@Thickness 0.126 in