Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
NYCOA 2038 10% Glass Filled Nylon 6 10% glass filled very high viscosity nylon 6Information provided by NYCOA, Inc. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CM6140 PC+ABS Cycoloy resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffnes.. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
Quadrant EPP Duratron® PEI U1000 LSG Polyetherimide, unfilled, extruded, Biocompatibility tested (ASTM Product Data Sheet) Duratron® U1000 (Formerly Ultem® 1000) polyetherimide is an amorphous, high-performance polymer with exceptional flame and heat resistance. It performs continuously to 340°F (171°C), making it.. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
Quadrant EPP Nylatron® MC® 901 Blue, Heat Stabilized, Type 6 (ASTM Product Data Sheet) Data provided by Quadrant Engineering Plastic ProductsBroadest size range availabilityGood mechanical and electrical propertiesIdeal balance of strength and toughnessCast as finished parts and near .. |
|||
Flexural Modulus | 3.45 - 9.65 GPa | 500 - 1400 ksi | Average value: 6.85 GPa Grade Count:31 |
Overview of materials for Polyphthalamide (PPA), 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are.. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | Tangent; ASTM D790 |
RheTech Products G20P252-01 20% Glass Fiber Reinforced Polypropylene Copolymer, Black Applications: Interior trimArm rest insertConsolesDome light housingInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
Ineos Nova 2504 General Purpose Crystal Polystyrene
(discontinued **) Good blending resin, Good balance of flow, strength and heat resistance, USP Class VI Applications: Consumer electronics, HousewaresExposure to gamma radiation in the 2.02-6.06 megarad range has no .. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
PolyOne Edgetek® AS-20GF/000 Acrylonitrile Butadiene Styrene (ABS) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for .. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
LNP Lubricomp® PDX-E-00548 CCS Polyetherimide, Aramid Fiber Reinforced, PTFE Lubricant
(discontinued **) Features: Lubricated, Low to None Ion ContentForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however man.. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
PolyOne Lubri-Tech™ NL-20GF/05T Nylon 6/12, Glass Filled, PTFE Lubricated
(discontinued **) Description/Features:Glass Fiber ReinforcedPTFE LubricatedInformation provided by PolyOne Corporation. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
Clariant Renol 612G10-L Nylon 612, 10% Glass Fiber Reinforced, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D-790 |
Axiall 5006 Rigid PVC, Extrusion, White Georgia Gulf 5006 White is a rigid PVC pellet compound designed for extrusion of rigid PVC house siding, window profiles and various contours where maximum weather resistance is required. Georgia G.. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
Polymer Resources PPX-G10 Modified PPO, 10% Glass Reinforced
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |