Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 8.80 GPa | 1280 ksi | 1.3 mm/min; ASTM D790 |
Ovation Polymers Opnyl OP6GF50 Nylon 6, 50% Glass Reinforced, Conditioned Nylon 6 - Glass reinforced (50 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m.. |
|||
Flexural Modulus | 8.80 GPa @Temperature 23.0 °C |
1280 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB SCANAMID 66.6 C12^F30 Nylon 66/6, Glass Fiber, Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 |
LATI LATILUB 88/50-20GRT K/10 PEEK Based, 10% Carbon Fiber Reinforced, 20% Graphite and PTFE Self Lubricating Plastic Latilub self-lubricating plastic materials are designed to replace metals in applications such as gears, bushings, cams, slides, etc., for which, besides their intrinsic properties (moldability, low.. |
|||
Flexural Modulus | 8.80 GPa @Temperature 23.0 °C |
1280 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB SCANMID 6 B13^ F30 Nylon 6, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ISO Value |
BASF Capron® 5233G 33% Glass-Filled Nylon 66 (Dry)
(discontinued **) Capron 5233G is a 33% glass fiber reinforced, polyamide 6,6 injection molding compound offering excellent strength, stiffness, creep resistance and dimensional stability. This balance of engineerin.. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ISO Value |
BASF Capron® 5233G HS BK-102 33% Glass-Filled Nylon 66 (Dry)
(discontinued **) Capron 5233G HS BK-102 is a 35% glass reinforced, heat stabilized, pigmented black nylon 6,6 injection molding compound offering excellent strength, rigidity, stiffness, creep resistance, and dimens.. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | 2mm/min; ASTM D790 |
Kingfa PA66-RG301 Flame Retardant, 30% Glass Fiber Reinforced PA66 Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesNo bloomingApplications:Injection moldingConnectorsRelayBobbinsPlugsInformation Provided by Kingfa Sci. & Tech.. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | 2mm/min; ASTM D790 |
Kingfa PBT-RG30 Flame Retardant, 30% Glass Fiber Reinforced PBT Features:Flame retardantHigh strengthHigh temperature propertiesOutstanding electrical propertiesGood heat resistanceApplications:Injection moldingConnectorsRelayBobbins, plugsE & E partsInformation.. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP EFL36E PEI (Europe-Africa-Middle East) LNP* Lubricomp* EFL36E is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Easy Molding. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36SXS PA 66 (Europe-Africa-Middle East) LNP* LUBRICOMP* RFL36SXS is a compound based on PA 66 resin containing Glass Fiber, PTFE. Added features include Internally Lubricated, Heat Stabilized. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON DE0029EF PC LNP STAT-KON* DE0029EF is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding. Flame Retardant, Electrically Conductive. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp DF0069E PC LNP* Thermocomp* DF0069E is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.This data was supplied by SABIC.. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 830 PBT (Europe-Africa-Middle East) VALOX 830 is a 30% glass fibre reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housing assemblies, industrial glue guns, appliance housings and handles. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 |
Plenco 2535 Phenolic, Granular, Compression Molded PLENCO 02535 is a general purpose, organic filled phenolic molding compound offering optimized cure characteristics and excellent electrical properties. Type ASTM 5948 CFG, and UL recognized under c.. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 |
Plenco 3356 Phenolic, Granular, Injection Molded PLENCO 03356 is a mineral filled phenolic molding compound offering excellent arc resistance, comparative tracking, and flame resistant properties. UL recognized under component file E40654. 03356 i.. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 |
Plenco 4466 Phenolic, Granular, Injection Molded PLENCO 04466 is a heat resistant, mineral and flock filled phenolic molding compound, offering excellent mechanical strength and cosmetic properties. UL recognized under component file E40654. 04466.. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ISO 178 |
Polyram PlusTek PA4501G6 Nylon 66, 30% Glass Fiber Reinforced, Low Friction 30% Glass fiber reinforced Nylon 66 for low friction applications.Information provided by Polyram. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ISO 178-93 |
Wellman Wellamid® GF33-66 XE-BKDX9 33% Glass Fiber Reinforced Nylon 66 Description: Glass Fiber Reinforced Nylon 66Information provided by Wellman. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | cond; ISO 178 |
DSM Novamid® 1013G45 1 NA PA6-GF45 45% Glass Reinforced, Injection Molding |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ISO 178 |
Eurostar Star L PA66 30V D51 PA66, Glass Fiber Filled, Injection Molded Star L PA66 30V D51 is a PTFE lubricated, Glass Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | 2 [mm/min]; ISO 178 |
Akro-Plastic Akromid® A3 GF 30 (2397) PA 6.6 Dry, 30% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 |
Adell AW-37 Nylon 66, 35% Glass Reinforced; Superior Finish Data provided by Adell Plastics, Inc. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ISO 178 |
Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Dry as Molded Vydyne® R633 is 33% glass-fiber reinforced, PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold .. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ISO 178 |
Ascend Performance Materials Vydyne® R633H Nylon 66/6, 33% Glass Reinforced, DAM Vydyne® R633H is 33% glass-fiber reinforced PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold .. |
|||
Flexural Modulus | 8.80 GPa @Temperature 23.0 °C |
1280 ksi @Temperature 73.4 °F |
DAM; ISO 178 |
DuPont Performance Polymers Zytel® 73G30TGI BK267 Nylon 6
(Unverified Data**) Zytel® 73G30TGI BK267 is a 30% glass fiber reinforced, toughened, black polyamide 6 optimized for gas injection molding process.Information provided by DuPont Performance Polymers |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | GB/9341 |
Zhejiang Juner PA-A6-6H High CTI Value Halogen-Free Environmental Protection Flame-Resistant and Reinforced Polyamide Applications: Circuit Breaker, BaseInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Flexural Modulus | 8.80 GPa | 1280 ksi | ISO 178 |
Kuraray Genestar™ G1300A-M41 Nylon, 30% Glass Filled Glass reinforced injection grade. Main Features:Chemical resistanceHeat resistanceExamples of applications:Gears and bearing retainersIntercooler tank and turbo duct pipe |