- Polymer Property : Flexural Modulus = 3.90 GPa
Polymer Property : Flexural Modulus = 3.90 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 3.90 GPa | 566 ksi | STN EN ISO 178 |
| Plastcom PLASTAMID® 66 GF 15 T 15 TS PA66 reinforced with glass fibers and mineral filler, heat stabilized Black PA66 for injection molding, reinforced with 15% glass fiber and 15% mineral filler, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of elect.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | |
| Plastcom SLOVAMID 6 GF 10 TS PA6, 10% glass fibre FeaturesPA 6 for injection moulding, chemically strengthened with 10% glass fibre. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Cycolac® INP572 ABS High molecular weight SAN, functions as a carrier resin for color concentrates. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to pro.. |
|||
| Flexural Modulus | 3.90 GPa @Temperature 23.0 °C |
566 ksi @Temperature 73.4 °F |
ISO 178 |
| Polykemi AB POLYfill PPH T15040CR Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| Nilit FRIANYL B63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Modulus | 3.90 GPa @Temperature 23.0 °C |
566 ksi @Temperature 73.4 °F |
ISO 178 |
| Polykemi AB SCANFILL FOIL ABYX52C1 PP/PE, Thermoforming Grade Information provided by Polykemi AB |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific) LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific) LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ASTM D790 |
| Shell Carilon® DB6G3A10 Polyketone, 15% Glass-Reinforced General-Purpose Injection Molding Grade
(discontinue Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DB6G3A10 is a 15 percent short glass-fiber-reinforced general-purpose injection molding grade with .. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| Solvay Specialty Polymers KetaSpire® KT-880 Polyetheretherketone (PEEK)
(Unverified Data**) KetaSpire KT-880 is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in pellet form. KetaSpire PEEK is produced to the highest industry standards and is characterized by a dist.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ASTM D790 |
| Solvay Specialty Polymers KetaSpire® KT-880P Polyetheretherketone (PEEK)
(Unverified Data**) KetaSpire KT-880P is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color coarse powder form. KetaSpire PEEK is produced to the highest industry standards and is.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | Result based on similar products; ISO 178 |
| Victrex® PEEK 150UF10 Polyetheretherketone Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, fine powder for composite manufacture, easy flow, FDA food contact compliant.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ASTM D790 |
| Asahi Kasei Tenac® GT525 Acetal Homopolymer, 25% Glass Beads
(discontinued **) 25% glass beads-filled grade with superior isotropic dimensional stability.Applications: Speedometer frames.This product is not a part of the standard product line dated 2003. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ASTM D790 |
| IRPC Polimaxx Polene 2311LCX TA6 Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE BLOCK COPOLYMER WITH 30% TALCUM REINFORCED, HIGH IMPACT STRENGTHAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | Tangent at 0.05 in/min; ASTM D790A |
| LyondellBasell Higlass SB224-3 Polypropylene Copolymer, 30% Glass Fiber Key Features: conventional melt flow, medium high modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, high impact strength, high stiffness, good processabilityApplications: .. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| Solvay Specialty Polymers KetaSpire® KT-880FP Polyetheretherketone (PEEK) KetaSpire® KT-880FP is the high-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural color fine powder form for compression molding and other uses that can benefit from th.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP Thermocomp AF0029 ABS (Europe-Africa-Middle East) LNP* THERMOCOMP* AF0029 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features include: Flame Retardant.This data was supplied by SABIC-.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ASTM D790 |
| Saint-Gobain Meldin® 7021 Isostatically Molded Graphite Filled Polyimide Melidin® 7021 is a self-lubricating thermosetting polyimide that contains 15% graphite filler. Melidin® 7021 has a low coefficient of friction and high heat resistance, and is best for high t.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP IB008 PA 6/12 (Europe-Africa-Middle East) LNP* Thermocomp* IB008 is a compound based on Nylon 6/12 resin containing Glass Bead. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT LNP* LUBRICOMP* WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible. |
|||
| Flexural Modulus | 3.90 GPa @Temperature 23.0 °C |
566 ksi @Temperature 73.4 °F |
|
| Hexcel® HexPly® 954-6 Curing Cyanate Resin HexPly® 954-6 is a 250°F (121°C) curing toughened cyanate resin with 300°F (149°C) Tg. HexPly® 954-6 is formulated for autoclave curing. Recommended cure is three hours at 250°F (121°C). Ser.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ASTM D790 |
| Clariant ABS4500G10BK ABS, 10% Glass Reinforced Data provided by Clariant Masterbatches |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| Ascend Performance Materials Vydyne® ECO315 BK13 Nylon 66, Flame Retardant, DAM Vydyne® ECO366 BK13 is a non-halogenated, unfilled, flame-retardant PA66 homopolymer designed with superior flow properties to assist in filling thin-walled, intricate parts. It is lubricated for m.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| Ascend Performance Materials Vydyne® ECO366 Nylon 66, Flame-retardant, DAM Vydyne® ECO366 is a non-halogenated, unfilled, flame-retardant PA66 homopolymer designed with superior flow properties to assist in filling thin-walled, intricate parts. It is lubricated for machin.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | DIN 53452; ASTM D790 |
| Kolon Kopa® KN173MS Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| Panjin Zhongrun Chemerize 021P Medium Viscosity CoPEEK Information provided by Bieglo Gmbh. |
|||