SABIC Innovative Plastics Cycolac® INP572 ABS

Category	Polymer , Thermoplastic , ABS Polymer
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Cycolac®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Cycolac® INP572 ABS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High molecular weight SAN, functions as a carrier resin for color concentrates. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direct weather exposure. Provides excellent melt strength for extrusion, blow molding, or thermoforming applicationsThis data was supplied by SABIC-IP for the Americas region.

Physical Properties	Metric	English	Comments
Specific Gravity	1.08 g/cc	1.08 g/cc	ASTM D 792
Density	1.08 g/cc	0.0390 lb/in³	ISO 1183
Melt Flow	5.8 g/10 min @Load 3.80 kg, Temperature 230 °C	5.8 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D 1238
	16 g/10 min @Load 10.0 kg, Temperature 220 °C	16 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	92.0 MPa	13300 psi	2 mm/min; ISO 178
	134 MPa	19400 psi	1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus	3.46 GPa	502 ksi	2 mm/min; ISO 178
	3.90 GPa	566 ksi	1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched	0.460 J/cm @Temperature 23.0 °C	0.862 ft-lb/in @Temperature 73.4 °F	ASTM D 256
Izod Impact, Notched (ISO)	2.00 kJ/m² @Temperature -30.0 °C	0.952 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
	3.00 kJ/m² @Temperature 23.0 °C	1.43 ft-lb/in² @Temperature 73.4 °F	80104; ISO 180/1A
Charpy Impact Unnotched	0.100 J/cm² @Temperature 23.0 °C	0.476 ft-lb/in² @Temperature 73.4 °F	ISO 179/2C

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C @Thickness 3.20 mm	203 °F @Thickness 0.126 in	unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	87.0 °C	189 °F	Flatw 80104 sp=64mm; ISO 75/Af
	85.0 °C @Thickness 3.20 mm	185 °F @Thickness 0.126 in	unannealed; ASTM D 648
Vicat Softening Point	102 °C	216 °F	Rate B/50; ISO 306
	105 °C	221 °F	Rate B/120; ISO 306