IRPC Polimaxx Polene 2311LCX TA6 Polypropylene Compound
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | IRPC Polimaxx |
| Trade Name | Polene |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | IRPC Polimaxx Polene 2311LCX TA6 Polypropylene Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CHARACTERISTICS: POLYPROPYLENE BLOCK COPOLYMER WITH 30% TALCUM REINFORCED, HIGH IMPACT STRENGTHAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength, Yield | 28.4 MPa | 4120 psi | ASTM D638 |
| Elongation at Break | 16 % | 16 % | ASTM D638 |
| Flexural Yield Strength | 43.1 MPa | 6260 psi | ASTM D790 |
| Flexural Modulus | 3.90 GPa | 566 ksi | ASTM D790 |
| Izod Impact, Notched | 0.461 J/cm @Temperature 23.0 °C |
0.863 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Pyrotek Pyroboard™ S1090 Roller
- Lanxess Durethan® BKV 35 H3.0 000000 Nylon 6, Glass Fiber Reinforced
- Haynes Hastelloy® C-22® alloy, 0% cold worked sheet
- SABIC Innovative Plastics Valox® 420 PBT (Asia Pacific)
- Trelleborg Fillite® FG (300) Alumino-silicate Cenospheres
- Trelleborg Emerson & Cuming Eccobond® A316-48 One-Component Fast Cure Epoxy Adhesive
- BASF Cyclopentanone
- 3M Scotchcal™ 1000LF-114 Graphic Film
Copyright © lookpolymers.com All Rights Reserved