Polymer Property : Flexural Modulus = 17.9 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	17.9 GPa @Temperature 23.9 °C	2600 ksi @Temperature 75.0 °F	Dry; ASTM D790
Park Electrochemical Nelcote® E-766B Epoxy Prepreg, 120 E-Glass Reinforced Nelcote® E-766B is a low tack, self adhesive epoxy resin system designed for honeycomb applications. E-766B displays excellent peel properties.Key Features and Benefits:Self adhesive resin system f..
Flexural Modulus	17.9 GPa @Temperature 23.9 °C	2600 ksi @Temperature 75.0 °F	Dry; 325°F Autoclave; ASTM D790
Park Electrochemical Nelcote® F-554 Phenolic Prepreg, Commercial Silica Fabric Reinforced Nelcote® F-554 is a high purity silica filled phenolic resin coated on Commercial or Aerospace grade silica fabric. F-554 is used in the manufacture of intermediate temperature ablative rocket nozz..
Flexural Modulus	17.9 GPa	2600 ksi	ASTM D790
Quantum Composites QC-8560 60% Glass Fiber Vinyl Ester SMC QC-8560 is a vinyl ester based sheet molding compound (SMC) designed for compression molding of components requiring high structural strength. It maintains excellent mechanical properties at temper..
Flexural Modulus	17.9 GPa	2600 ksi	1.3 mm/min; ASTM D790
PolyOne Edgetek® PS-30CF/000 HF UV BLACK Polybutylene Terephthalate (PBT) Information provided by PolyOne
Flexural Modulus	17.9 GPa	2600 ksi	ASTM D790
Solvay Specialty Polymers KetaSpire® KT-880 CF30 Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-880 CF30 is a high flow, 30% carbon fiber reinforced grade of polyetheretherketone (PEEK). Carbon-fiber reinforcement of KetaSpire PEEK provides the maximum levels of mechanical propert..
Flexural Modulus	17.9 GPa	2600 ksi	ASTM D790
Solvay Specialty Polymers AmodelÂ® A-1565 HS Polyphthalamide (PPA), 65% GlassMineral (Dry) AmodelÂ® A-1565 HS is a 65% glass and mineral-reinforced polyphthalamide (PPA) designed to be cost-effective in applications requiring high stiffness, good dimensional stability and good retention..
Flexural Modulus	17.9 GPa	2600 ksi	ASTM D790
Techmer ES ElectrafilÂ® J-1/CF/30/TF/15 Nylon 66, 30% Carbon Fiber Reinforced, PTFE Lubed Carbon Fiber Reinforced, PTFE Lubricated
Flexural Modulus	17.9 GPa	2600 ksi	ASTM D790
Solvay Specialty Polymers KetaSpireÂ® KT-880 CF30 Polyetheretherketone (PEEK), 30% Carbon Fiber KetaSpireÂ® KT-880 CF30 is a high flow, 30% carbon fiber reinforced grade of polyetheretherketone (PEEK). Carbon-fiber reinforcement of KetaSpireÂ® PEEK provides the maximum levels of mechanical..
Flexural Modulus	17.9 GPa	2600 ksi	ASTM D790
Techmer ES LuriblendÂ® PA4/6 CF30 TL10 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(10%)Features: LubricatedTPCI# 8661150Information provided by TP Composites, ..
Flexural Modulus	17.9 GPa	2600 ksi	ASTM D790
Techmer ES LuriblendÂ® PA6/6 CF33 ML2 BK 33% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 33% Filler by WeightAdditive: Molybdenum Disulfide LubricantFeatures: Lubricated, Low Friction and Good Wear ResistanceAp..
Flexural Modulus	17.9 GPa	2600 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RX12402 PA 66 LNP* Thermocomp* RX12402 is a compound based on PA66 containing 60% Glass Fiber. Added feature is Superior Flow.
Flexural Modulus	17.9 GPa	2600 ksi	90° stress angle
Cytec Cyply® 1002 Epoxy Fiberglass Composite, Isotropic CYPLY® 1002 is a cured epoxy composite material based on a unique non-woven parallel filament construction. This type of construction minimizes filament stress abrasion that can shorten fatigue li..
Flexural Modulus	17.9 GPa	2600 ksi	ASTM D790
Clariant Renol PA111G60 Nylon 66, 60% Glass Fiber Data provided by Clariant Masterbatches
Flexural Modulus	17.9 GPa	2600 ksi	ASTM D790
E-Polymers TEKASTER® F615G55 55% Glass Fiber Reinforced High Modulus PET Polyester Resin: TEKASTER is thermoplastic polyester resins (PBT, PET) mostly injection molding. PBT has excellent mechanical properties and well balanced engineering plastics with an electrical pe..