Park Electrochemical Nelcote® E-766B Epoxy Prepreg, 120 E-Glass Reinforced

Category	Polymer , Thermoset , Epoxy
Manufacturer	Park Electrochemical Corp.
Trade Name	Nelcote®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Park Electrochemical Nelcote® E-766B Epoxy Prepreg, 120 E-Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Nelcote® E-766B is a low tack, self adhesive epoxy resin system designed for honeycomb applications. E-766B displays excellent peel properties.Key Features and Benefits:Self adhesive resin system for sandwich panel applicationsFlame retardant and self-extinguishingLow tack and long out-times for ease of processingApplications/Qualifications:Sandwich panels / structuresAircraft InteriorsMass Transit InteriorsInformation provided by Park Electrochemical Corp.

Physical Properties	Metric	English	Comments
Volatiles	<= 1.0 % @Temperature 163 °C	<= 1.0 % @Temperature 325 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	379 MPa @Temperature 23.9 °C	55000 psi @Temperature 75.0 °F	ASTM D638
Tensile Modulus	17.9 GPa @Temperature 23.9 °C	2600 ksi @Temperature 75.0 °F	Dry; ASTM D638
Flexural Strength	552 MPa @Temperature 23.9 °C	80000 psi @Temperature 75.0 °F	Dry; ASTM D790
Flexural Modulus	17.9 GPa @Temperature 23.9 °C	2600 ksi @Temperature 75.0 °F	Dry; ASTM D790
Compressive Strength	400 MPa @Temperature 23.9 °C	58000 psi @Temperature 75.0 °F	Dry; ASTM D695
Compressive Modulus	18.6 GPa @Temperature 23.9 °C	2700 ksi @Temperature 75.0 °F	Dry; ASTM D695
Shear Strength	56.5 MPa @Temperature 23.9 °C	8200 psi @Temperature 75.0 °F	Short-Beam, Dry; ASTM D2344

Thermal Properties	Metric	English	Comments
Glass Transition Temp, Tg	93.0 °C	199 °F	Dry; DMA

Processing Properties	Metric	English	Comments
Shelf Life	12.0 Month @Temperature -17.8 °C	12.0 Month @Temperature 0.000 °F

Descriptive Properties	Value	Comments
Fabric Area Weight (g/m²)	107
Prepreg Resin Content (%)	50-60
Resin Flow (%)	20-30	275°F, 15psi