Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 13.0 GPa | 1890 ksi | 1.3 mm/min; ASTM D790 |
Ovation Polymers Opnyl OP66GF50 Nylon 66 Nylon 66-Glass reinforced(50%), high tensile strength, stiffness and HDT.Information provided by Ovation Polymers |
|||
Flexural Modulus | 13.0 - 16.0 GPa | 1890 - 2320 ksi | Compression; ISO 178 |
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy.. |
|||
Flexural Modulus | 13.0 - 16.0 GPa | 1890 - 2320 ksi | Injection; ISO 178 |
Raschig Group RALUPOL® 4806 UP Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80.. |
|||
Flexural Modulus | 13.0 - 16.0 GPa | 1890 - 2320 ksi | Injection; ISO 178 |
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | |
Cookson Group Plaskon® S-7S Epoxy Encapsulant
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A low stress, low viscosity epoxy encapsulant designed for packaging stress-sensitive semiconductor devices. It is specifically .. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | |
Lehmann & Voss LUVOCOM® 1105-8169 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Dynamic stressed parts at high movement velocity.High chemical resista.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | |
Lehmann & Voss LUVOCOM® 1301/CF/15/TF/5 BK PPS, linear, with carbon fiber and PTFE Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.High-strength and stiff parts w.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
IDI Composites A-207 Thermoset Polyester, Sheet AUTOMOTIVE - Versatile family of compounds specifically designed for automotive structural applications. Low shrink characteristics, heat resistance, long-term dimensional stability, and corrosion r.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
IDI Composites C-204 Thermoset Polyester, Sheet CORROSION - (Patent pending). Versatile family of compounds designed for pressurized and thermo-mechanically stressed applications. Excellent corrosion resistance and high strength.Data provided by .. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
IDI Composites M-106 Thermoset Polyester, Molding Mechanical grade materials in a range of strengths with excellent moldability and molded part appearance.Data provided by the manufacturer. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
IDI Composites M-205 Thermoset Polyester, Sheet MECHANICAL - Versatile family of compounds designed to meet a variety of mechanical, electro-mechanical, and corrosion applications. Outstanding structural properties at lowest possible costs.Data p.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® MKD-1015 PA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
Sumitomo Bakelite North America E 3812M-1 Mineral and Glass Filled Electrical Encapsulation Grade Epoxy E 3812M-1 is a mineral and short fiberglass filled epoxy molding compound for low pressure encapsulation molding, featuring excellent dimensional stability, good thermal shock resistance, and good e.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 |
SABIC Innovative Plastics LNP VERTON RVL28 PA 66 LNP* VERTON* RVL28 is a compound based on Nylon 66 resin containing 40% Long Glass Fiber, 10% PTFE. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant, Structura.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
Toyobo VYLOPET® EMC130-20 Injection Molding Polyester Resin, Flame Resistant Applications: Relay partsFeatures: Excellent arc resistanceFlame resistanceInformation provided by Toyobo. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 |
Polyram RamSter PF300G9 PBT, 45% Glass Fiber 45% Glass fiber reinforced PBT for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | |
Cytec Thornel® Graphite Cloth Laminate with Mil R-9299 Resin Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
Ensinger TECATRON™ GF 40 Polyphenylene sulfide (PPS) TECATRON PPS is a high performance thermoplastic that combines good mechanical properties with excellent thermal and chemical resistance properties. There is no known solvent that dissolves TECATRON.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | DAM; ISO 178 |
DuPont Performance Polymers Zytel® HTN 92G45DH2 BK083 Polyphthalamide (PPA) 35% Glass Reinforced PPA High Performance Polyamide with DuPont Zytel HTN92G45DH2 BK083 is a 45% glass reinforced high performance polyamide resin using DuPont SHIELD Technology with high flow and e.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
A. Schulman ComAlloy Comtuf® 463 Glass Reinforced, Impact Modified, PBT Alloy Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 |
Vyncolit W5020 Glass Filled Novolac Phenolic Novolac resin based, glass fiber and glass bead reinforced. High dimensional stability and excellent chemical resistance at high temperatures in hydraulic brake fluids. Used in the ABS system.Inform.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | DIN 53 457 |
Albis Plastics Tedur® L 9510-1 PPS, 40% Glass Fiber High Strength, High Rigidity Standard Grade. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Pump Impellers, Valve Housings and BushingsProcessing: Injection Molding (.. |
|||
Flexural Modulus | 13.0 - 16.0 GPa | 1890 - 2320 ksi | Injection; ISO 178 |
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
Chevron Phillips Xtel® XK2240 Polyphenylene Sulfide Alloy
(discontinued **) Natural Color Polyphenylene Sulfide AlloyXtel™ XK2240 is a high performance, glass fiber reinforced, PPS-based alloy developed to provide excellent mechanical strength with an unique blend of tough.. |
|||
Flexural Modulus | 13.0 GPa @Thickness 3.20 mm |
1890 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUXY KS G55 Amorphous PA6 Description: Injection Molding, Amorphous PA6, High Modulus, High Impact, Low WarpageApplication: Electric/Electronic Components (LCD Bracket)Information provided by LG Chemical |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
Owens Corning Glass Fiber Reinforced Polyphenylene Sulfide, 40 wt.% glass Polyphenylene Sulfide provides excellent resistance to organic solvents (below 375°F). It is unaffected by strong alkalis or aqueous organic salt solutions. Data provided by the manufacturer, Owen.. |
|||
Flexural Modulus | 13.0 GPa @Temperature 60.0 °C |
1890 ksi @Temperature 140 °F |
ASTM D790 |
LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS)
(Unverified Data**) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |
|||
Flexural Modulus | 13.0 GPa | 1890 ksi | |
Lehmann & Voss LUVOCOM® 1301/CF/15/TF/5-1 PPS, linear, with carbon fiber and PTFE Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.High-strength and stiff parts w.. |