Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
Quadrant EPP TIVAR® 1000 UV Stabilized UHMW, Black (ASTM Product Data Sheet) |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
Quadrant EPP TIVAR® 1000 UV Stabilized UHMW-PE, Natural & Colored Except Black (ASTM Product Data Sheet) |
|||
Flexural Modulus | 0.800 GPa @Temperature 90.0 °C |
116 ksi @Temperature 194 °F |
ASTM D790 |
Nilit Polynil® P50L Externally Lubricated Nylon 66 Description: Polynil P50L is a general purpose injection molding grade that is widely used for gears, bearings, fasteners, clips. It is also suited for monofilament extrusion.Key characteristics: Ex.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | Conditioned; ISO 178 |
Lanxess Durethan® B 40 SK 000000 Nylon 6 PA 6, non-reinforced, injection molding |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
Solvay TECHNYL® C 230 PA6, Conditioned Description: Unreinforced polyamide PA6, with improved impact resistance, for injection molding.Available in: EuropeProduct Applications: This grade has improved impact strength and higher flexibili.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
Borealis BorPURE™ RE216CF Polypropylene Random Copolymer BorPure™ RE216CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films for metallization. Applications: BorPure™ RE216CF is recommended for Lamination films, Me.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | 2mm/min; ISO 178 |
Borealis RA130E-1498 Polypropylene Random Copolymer RA130E-1498 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is white colored. Applications: RA130E-1498 is recommended for the production of PP-R p.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | 2mm/min; ISO 178 |
Borealis RA130E-6015 Polypropylene Random Copolymer RA130E-6015 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is green colored. Applications: domestic water, heating, relining, plumbing, and indust.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | 2mm/min; ISO 178 |
Borealis RA130E-6034 Polypropylene Random Copolymer RA130E-6034 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is green colored. Applications: domestic water, heating, relining, plumbing, and indust.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
Unipetrol PE HD LITEN® MS 57 HDPE Made for injection molding applications.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
Unipetrol PE HD LITEN® VL 10 HDPE Extrusion and pipe applications.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D 790 |
Total 3802 B HDPE, cable, sheet, pipe, injection molding FINATHENE® 3802 B is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low-pressure slurry polymerization process. FINATHENE® 3802 B is a black polyethylene.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
A. Schulman POLYFORT™ PP 1329 UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1329HU is a high flow UV stabilized, medium impact copolymer polypropylene. Information provided by A. Schulman. |
|||
Flexural Modulus | >= 0.800 GPa | >= 116 ksi | ASTM D 790 |
Cossa Polimeri ESTAPROP KUR 1010 TG05 Polypropylene, 5% Mineral Filled PP copolymer 5% mineral fillerElastomer modified, very high impact strength at low temperatureInformation provided by Cossa Polimeri S.r.l. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
Ecomass® 4703TU95 Tungsten Filled Polyurethane Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applicationsHigh Specific GravityTungsten Powder Filled Polyurethane (TPU)FlexibleInformation provided by Technical Po.. |
|||
Flexural Modulus | 0.800 GPa @Temperature 120 °C |
116 ksi @Temperature 248 °F |
ISO 178 |
DSM Stanyl® TS300 PA46 |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO R178 |
Arkema Group ORGASOL® 3502 D Nat 1 Copolyamide 6/12 Information provided by Arkema Group |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
Aclo Accucomp Polyethylene HD0202L High Density |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0437C20L1 Calcium Reinforced |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM-D790 |
Braskem RP 344 RACO Random Polypropylene Copolymer RP 344 is a medium melt flow rate random copolymer. It is suitable for blown and cast film extrusion and features good processability, excellent optical properties, and outstanding sealability. Its .. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM-D790 |
Braskem Symbios 3102 Polypropylene Terpolymer Braskem Symbios 3102 is a medium melt flow rate terpolymer with a heat seal temperature below 110ºC on its non-treated face. It is designed for use as a heat sealing layer for cast film coextrusion.. |
|||
Flexural Modulus | >= 0.800 GPa | >= 116 ksi | ASTM D790 |
Buckeye Polymers BP HDPE 9610 R RLK High Density Polyethylene Product Information: Our HDPE grade of materials are designed to offer excellent physical properties while providing cost savings versus higher cost prime equivalents. Buckeye Polymers HDPE materia.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | SAE J949 |
Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (4.5 mm Molded Thickness) AZDEL SuperLite® SL551000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
Buckeye Polymers BP Flex D7030 UC85 TPO Bumpers, Air damsTPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment. These resins have excellent UV resi.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
Cathay PA56 Renewable Engineering Polyamide, 50% RH Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | 2mm/min; ASTM D790 |
3M Dyneon™ PVDF 31008/0003 Polyvinylidene Fluoride
(discontinued **) 3M™ Dyneon™ PVDF 31008/0003 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. Dyneon PVDF 31008/0003 also has a very low brittleness temperatu.. |
|||
Flexural Modulus | 0.800 GPa @Temperature 120 °C |
116 ksi @Temperature 248 °F |
ISO 178 |
DSM Stanyl® TE300 PA46 Heat Stabilized |
|||
Flexural Modulus | 0.800 - 3.40 GPa @Temperature 60.0 - 120 °C |
116 - 493 ksi @Temperature 140 - 248 °F |
Average value: 2.45 GPa Grade Count:4 |
Overview of materials for Polypropylene with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are i.. |