Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.600 - 0.600 GPa @Temperature 90.0 - 90.0 °C |
87.0 - 87.0 ksi @Temperature 194 - 194 °F |
Average value: 0.600 GPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Flame Retardant". Each property range of values reported is minimum an.. |
|||
Flexural Modulus | 0.600 GPa @Temperature 175 °C |
87.0 ksi @Temperature 347 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® AP-9240 NL Polyphthalamide (PPA) Resin, 40% Mineral Filled, Dry as Molded
( AMODEL AP-9240 NL resin is a 40% mineral-filled, impact-modified polyphthalamide (PPA). It was designed to provide a smooth molded surface suitable for many decorative applications. This resin offer.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
NOVA Chemicals Sclair® 2508-UV9 MDPE Injection Molding Resin
(discontinued **) Features: Excellent processability for applications requiring stiffness and toughness, good cold temperature impact properties.Applications: Roll-out cart lids.Data provided by the manufacturer. |
|||
Flexural Modulus | 0.600 - 0.650 GPa | 87.0 - 94.3 ksi | |
Solvay Specialty Polymers Hyflon® PFA 450 Fluoropolymer
(discontinued **) Data provided by the manufacturer.Hyflon® PFA 450 has outstanding physical and chemical properties typical of fluoropolymers.Hyflon® PFA 420 |
|||
Flexural Modulus | 0.600 - 7.70 GPa | 87.0 - 1120 ksi | Average value: 4.41 GPa Grade Count:50 |
Overview of materials for Nylon 6, 30% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are includ.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | 1.3 mm/min; ASTM D790 |
ICO Polymers ICORENEâ„¢ 115-1332 LMDPE Rotational Molding Resin Description: ICORENE 115-1332 is a linear medium density polyethylene developed for use in rotational molding. It is an easy processing material with good surface gloss, scratch resistance and gene.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | 1.33 mm/min; ASTM D790 |
ICO Polymers ICORENEâ„¢ 190-1332 LMDPE Rotational Molding Resin Description: ICORENE 190-1332 is a compounded linear density polyethylene copolymer developed for rotational molding. It has a good balance of properties such as toughness, easy flow and stiffness.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Guarniflon MFA Fluoropolymer It’s a semi-crystalline fully-fluorinated melt processable fluoropolymer which offer the highest temperature rating and broadest chemical resistance of all melt processable fluoropolymers. It .. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Guarniflon PFA Perfluoroalkoxy Polymer Fluorinated thermoplastic material, offers the advantages of being thermo-processed whilst at the same time having the properties of PTFE, with excellent chemical and mechanical resistance for appli.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ISO 178 |
Solvay TECHNYL® C 52G4 MZ25 PA6, 25% mineral filler, DRY Description: TECHNYL® C 52G4 MZ25 is a 25% mineral reinforced melamine cyanurate flame retarded polyamide 6.This product is heat stabilized and is suitable for injection molding. This product is .. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP 2X03624H FP-F (FEP) LNP* THERMOCOMP* 2X03624H is a compound based on FEP resin containing Proprietary Filler(s). |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | 50% humidity; ISO 178 |
Borealis Borseal™ RE239CF Polypropylene Copolymer Borseal™ RE239CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films for metallization. Applications: Borseal™ RE239CF is recommended for food packaging, high.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Borealis Borstar® ME6053 Black Bimodal MD Polyethylene Compound for Jacketing of Communication and Power Cables Borstar ME6053 is a natural, bimodal medium-density polyethylene compound produced using the Borstar process. It is characterized by its tailor made properties important in jacketing applications, .. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ISO 178 |
Unipetrol PE HD LITEN® FB/FL 20 HDPE Made for tubular film and special applications.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ISO 178 |
Unipetrol PE HD LITEN® SB/SL 20 HDPE Made for blow molding, tubular film and special applications.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D 790 |
Total Lumicene® M 3410 EP HDPE Film, sheet FINACENE® M 3410 EP is a medium density metallocene based polyethylene resin. FINACENE® M 3410 EP is especially dedicated to film applications where a higher rigidity, good transparency and shrink.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D 790 |
Total Lumicene® mPE M 3410 EP HDPE Film Outstanding clarity and gloss; excellent bubble stability; excellent tear strength; high puncture resistance; good stiffness; excellent heat sealing properties; excellent compatibility with LDPE and.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ISO 178 |
Chengdu Polyster H8570Y Thermoplastic Polyether-ester Elastomer (TPEE) High modulus molding and injection grade. Contains improved color- stable antioxidants. Low frictional coefficient and good abrasion resistance. Applications requiring high strength, high toughness .. |
|||
Flexural Modulus | 0.600 GPa @Temperature 160 °C |
87.0 ksi @Temperature 320 °F |
ISO 178 |
DSM Stanyl® TW341-B PA46 Heat Stabilized, Lubricated |
|||
Flexural Modulus | 0.600 GPa @Temperature 160 °C |
87.0 ksi @Temperature 320 °F |
ISO 178 |
DSM Stanyl® TW341-N PA46 Heat Stabilized, Lubricated |
|||
Flexural Modulus | 0.600 GPa @Temperature 65.0 °C |
87.0 ksi @Temperature 149 °F |
ASTM Test |
BASF Ultramid® 8202C HS PA6 (Dry) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also.. |
|||
Flexural Modulus | 0.600 GPa @Temperature 65.0 °C |
87.0 ksi @Temperature 149 °F |
ASTM Test |
BASF Ultramid® 8202C PA6 (Dry) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Chem Polymer Chemlon 256 Nylon 6, Wire Jacketing Grade A non-halogenated, Allwires rated wire coating grade used primarily on cables for power and control circuits in commercial and industrial applications. The cables are oil, gasoline, and abrasion re.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Asahi Glass Fluon® P-62XP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | 1% secant; ASTM D790 |
ExxonMobil LL 8360 Rotational Molding Resin
(discontinued **) LL 8360 is a linear low density hexene copolymer designed to provide good processability along with outstanding dimensional control and low warpage. This resin is ideally suited for applications tha.. |
|||
Flexural Modulus | 0.600 - 0.600 GPa @Temperature 90.0 - 90.0 °C |
87.0 - 87.0 ksi @Temperature 194 - 194 °F |
Average value: 0.600 GPa Grade Count:1 |
Overview of materials for Nylon 6, Nucleated This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Nucleated". Each property range of values reported is minimum and maximum values of appropriate.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | SAE J949 |
Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness) AZDEL SuperLite® SL551400-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ISO 178 |
Unitika EX-1030 PA6, Conditioned High-impact nylonInformation provided by Unitika Ltd. |
|||
Flexural Modulus | 0.600 - 6.83 GPa @Temperature 100 - 175 °C |
87.0 - 991 ksi @Temperature 212 - 347 °F |
Average value: 2.98 GPa Grade Count:4 |
Overview of materials for Polyphthalamide (PPA), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Mineral Filled". Each property range of values reported is minimum and maximum values o.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | |
Kraton® D1102 + PP blend (50/50) Unmodified polypropylene has high rigidity and good heat resistance, but poor impact resistance, especially at low temperatures. Blending KRATON D and G polymers with PP significantly improves the .. |