SABIC Innovative Plastics LNP THERMOCOMP 2X03624H FP-F (FEP)
| Category | Polymer , Thermoplastic , Fluoropolymer , FEP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 2X03624H FP-F (FEP).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* 2X03624H is a compound based on FEP resin containing Proprietary Filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.22 g/cc | 0.0802 lb/in³ | ISO 1183 |
| 2.23 g/cc | 0.0806 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0389 cm/cm @Time 86400 sec |
0.0389 in/in @Time 24.0 hour |
ISO 294 |
| 0.039 cm/cm @Time 86400 sec |
0.039 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0449 cm/cm @Time 86400 sec |
0.0449 in/in @Time 24.0 hour |
ISO 294 |
| 0.045 cm/cm @Time 86400 sec |
0.045 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 13.0 MPa | 1890 psi | ASTM D638 |
| 14.0 MPa | 2030 psi | ISO 527 | |
| Elongation at Yield | 7.2 % | 7.2 % | ISO 527 |
| 9.3 % | 9.3 % | ASTM D638 | |
| Flexural Strength | 13.0 MPa | 1890 psi | ASTM D790 |
| 16.0 MPa | 2320 psi | ISO 178 | |
| Flexural Modulus | 0.600 GPa | 87.0 ksi | ISO 178 |
| 0.620 GPa | 89.9 ksi | ASTM D790 | |
| Izod Impact, Notched | 5.66 J/cm | 10.6 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 64.0 kJ/m² | 30.5 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 30.0 J | 22.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 46.0 J | 33.9 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 121 µm/m-°C @Temperature -40.0 - 40.0 °C |
67.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 121 µm/m-°C @Temperature -40.0 - 40.0 °C |
67.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 126 µm/m-°C @Temperature -40.0 - 40.0 °C |
70.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 128 µm/m-°C @Temperature -40.0 - 40.0 °C |
71.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 53.0 °C @Thickness 3.20 mm |
127 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Oxford Polymers C-Acetal -30GF-Natural Acetal Copolymer, 30% Glass Fiber Reinforced
- DuPont™ Clysar® RS900 Polyolefin Shrink Packaging Film, 60 Gauge (discontinued **)
- Huntsman HY 847 Cycloaliphatic Amine
- FKuR Kunststoff Bio-Flex® F 6510 Compostable PLA Blend
- SABIC Innovative Plastics LNP LUBRICOMP WFL34 PBT
- Dow DNDA-7147 NT 7 Linear Low Density Polyethylene Resin
- CLAL-MSX NICLAFOR® 1000 TF Quenched/Precipitation Heat Treated, Drawn Copper Alloy
- Fainplast Compounds HAX HF 039/31 Halogen Free PVC
- Americas Styrenics STYRON A-TECH® 1400AS High Impact Polystyrene
- Wellman Wellamid® FRGF1850-N1 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved