Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
Nylene® Naxel™ A914 Polycarbonate/ABS Alloy Description: Naxel™ A914 is a Polycarbonate/ABS alloy. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D882 |
SABIC Innovative Plastics Lexan® FR66 Polycarbonate Film, Flame Retardant Lexan FR66 flame-retardant film is a clear, thin-gauge polycarbonate film with a suede finish on one side and a matte finish on the other, and a UL94 V-0 listing to meet the stringent requirements i.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D882 |
SABIC Innovative Plastics Lexan® FR83 Polycarbonate Film, Flame Retardant Lexan* FR83 flame-retardant film is a matt/polished, thin-gauge polycarbonate film with a UL94 VTM-0 listing to meet the stringent requirements in a wide range of electrical, electronic and transpor.. |
|||
Tensile Strength, Ultimate | 60.0 - 225 MPa @Temperature 60.0 - 230 °C |
8700 - 32600 psi @Temperature 140 - 446 °F |
Average value: 107 MPa Grade Count:5 |
Overview of materials for Polyphthalamide (PPA), 50% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 50% Glass Fiber Reinforced". Each property range of values reported is minimum and maxi.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D882 |
SABIC Innovative Plastics Lexan® FR60 Polycarbonate Film, Flame Retardant Lexan FR60 flame-retardant film is a clear, thin-gauge polycarbonate film with polished surfaces on both sides, and a UL94 V-0 listing to meet the stringent requirements in a wide range of electrica.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ISO 527 |
LATI LATILUB 82-01M Nylon 12 Base, 1% Molybdenum Disulfide Self Lubricating Plastic
(discontinued **) Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri.. |
|||
Tensile Strength, Ultimate | 60.0 - 250 MPa | 8700 - 36300 psi | Average value: 131 MPa Grade Count:27 |
Overview of materials for Nylon 12, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Tensile Strength, Ultimate | 60.0 - 140 MPa | 8700 - 20300 psi | Average value: 110 MPa Grade Count:30 |
Overview of materials for Nylon 12, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM data at 5 mm/min. |
BASF Capron® 8202C HS Nylon 6 (Conditioned)
(discontinued **) Capron 8202C HS is a heat stabilized, low viscosity, polyamide 6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It i.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | DIN 53455; ASTM D638 |
Kolon NOPLA® KE831 PEN-PET Copolyester NOPLA® is an advanced PEN-PET copolyester which can be used for bottle, sheet & injection molding applicationsUV protection & prolonged outdoor durability, enhanced gas barrier, outstanding impac.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
LG Chemical Lupoy 1200-22 Polycarbonate Resin Description: LUPOY PC 1200-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
LG Chemical Lupoy 3010-22 Polycarbonate Resin Description: LUPOY PC 3010-22 resin is designed for injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Character.. |
|||
Tensile Strength, Ultimate | 60.0 MPa @Temperature 22.0 °C |
8700 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 2500 Unsaturated Polyester UP SMC 2500 is a special SMC for high voltage isolating applications. The glass level has been selected to combine good mouldability with good strength and stiffness properties. Even without a specific.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | |
Saint-Gobain Micaver® Glass-Mica Electrical Insulator, Compression Moldings Glass-mica compound that occupies a place between plastics and ceramics in terms of usage temperature. It can be molded and machined like plastics and has the mechanical properties (strength, hardn.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | 5mm/min; ISO 527 |
Styrolution Terblend® N NG-04 20% Glass Filled ABS/PA6 (Conditioned) Terblend N NG-04 is a glass fibre reinforced ABS/PA6 blend with excellent dimensional stability, low mold shrinkage and high heat resistance.Information provided by STYROLUTION, which is a joint ven.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
Plenco 4548 Phenolic, Granular, Transfer Molded PLENCO 04548 is a heat resistant mineral filled phenolic molding compound, offering fast cure rates and hot rigidity. Type ASTM 5948 CFG, and UL recognized under component file E40654. 04548 is avai.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ISO 527-1, 2 |
Polyplastics Duranex® 200FP Polybutylene Terephthalate (PBT), Unfilled PBT for film, Extrusion, Super High Flow DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
Covestro Makrolon® 2205 Polycarbonate, Injection Grade Exceptionally good flow injection molding grade with easy mold release, for parts with a low wall thickness and long flow paths.Information provided by Bayer.As of 1 September 2015, Bayer MaterialSc.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
DSM Arnite® B600SE PBT FR Flame Retardant |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | |
Covestro Makrolon® 8025 Polycarbonate High viscosity extrusion and injection molding grade with 20% short glass fibers and easy mold release, low anisotropy, for stiff moldings requiring good dimensional stability.Information provided b.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8260 HS PA6 (Conditioned) |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ATSM D638 |
Ashley Polymers Ashlene® 525LD Nylon 66 High impact Nylon 66 with good stiffness, for injection molding.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 60.0 MPa @Temperature 760 °C |
8700 psi @Temperature 1400 °F |
|
ATI Allegheny Ludlum AL 453™ Stainless Steel Single phase iron-chromium ferritic stainless steel alloy. Should be annealed between 1450 and 1600°F and quickly cooled. Information provided by Allegheny Ludlum |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 662 Nylon 6, Glass Bead Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Glass Bead Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM data at 5 mm/min. |
BASF Capron® 8253 Impact Modified Nylon 6 (Conditioned)
(discontinued **) Capron 8253 is an unfilled type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Capron 8253 HS) and/or pigmented versions.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ATSM D638 |
Ashley Polymers Ashlene® PC/ABS Alloy 307WO General purpose flame retardant with high impact, good low temperature properties and high heat resistance.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
Chevron Phillips Ryton® PR09-60 Polyphenylene Sulfide Compound
(discontinued **) Polyphenylene Sulfide CompoundRyton® PR09-60 is pelletized unfilled high molecular weight polyphenylene sulfide resin suitable for extrusion or injection molding.Comments: Test specimen molding con.. |
|||
Tensile Strength, Ultimate | 60.0 - 75.0 MPa @Temperature 130 - 175 °C |
8700 - 10900 psi @Temperature 266 - 347 °F |
Average value: 69.4 MPa Grade Count:2 |
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea.. |
|||
Tensile Strength, Ultimate | 60.0 - 120 MPa | 8700 - 17400 psi | Average value: 89.8 MPa Grade Count:13 |
Overview of materials for Polystyrene + Polyphenylene Ether, Glass Filler This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene + Polyphenylene Ether, Glass Filler". Each property range of values reported is minimum and .. |