Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plaskolite Optix® CA-51 General Purpose Acrylic Resin Injection Molding and Extrusion Grade Pellets. Medium heat resistance and medium flow. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | 5 mm/min; parallel to flow; ASTM D638 |
Asahi Kasei Tenac® LA531 Acetal Homopolymer, High Lubricity
(discontinued **) High-lubricity block copolymer with excellent friction and wear characteristics, especially on POM.Applications: Gears, keyboard parts.This product is not a part of the standard product line dated 2.. |
|||
Tensile Strength, Ultimate | 56.0 MPa @Temperature 60.0 °C |
8120 psi @Temperature 140 °F |
ISO 527 |
LATI LASULF Polysulfone (PSU)
(Unverified Data**) Description: Lasulf products are composed of polysulfone (PSU). They feature good thermal and mechanical properties such as excellent toughness, even at low temperatures, excellent dimensional stabi.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 308 Black (INJ) Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok 308 is a two-stage, mineral and flock-filled phenolic molding compound designed to withstand the hostile environment of high abrasion and high tangential speed of engine pulleys. It is char.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 309 Black (INJ) Mineral/Fiber Filled Phenolic Molding Compound
(discontinued **) Plaslok 309 is a two-stage, mineral and fiber-filled phenolic molding compound having excellent impact strength; and as such, is considered a good candidate for replacing chopped-fiber filled compou.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plaslok 309 Black (INJ) Mineral/Fiber Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 309 is a two-stage, mineral and fiber.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
LG Chemical Lupoy 1603-06 Polycarbonate Resin Description: LUPOY PC 1603-06 resin is designed for extrusion products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Characteristics: .. |
|||
Tensile Strength, Ultimate | 56.0 MPa @Temperature 22.0 °C |
8120 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 0800 Unsaturated Polyester UP SMC 0800 is a special SMC for applications within househould and kitchenware. The glass level has been selected to combine good mouldability with good strength and stiffness properties. The product .. |
|||
Tensile Strength, Ultimate | 56.0 MPa @Temperature 22.0 °C |
8120 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 1650 Unsaturated Polyester UP SMC 1650 is a specially designed anti-microbial polyester moulding compound which incorporates a "germ killer" . It has been tested and found to be compliant for resistance to fungal defacement in .. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 00755 Melamine-Phenolic, Granular, Compression Molded PLENCO 00755 is a melamine-phenolic copolymer molding compound offering excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 00755.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 2369 Phenolic, Granular, Compression Molded PLENCO 02369 is a general purpose, organic filled phenolic molding compound, formulated to minimize the generation of free ammonia for applications that are sensitive to such formation. PLENCO 02369.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 2535 Phenolic, Granular, Injection Molded PLENCO 02535 is a general purpose, organic filled phenolic molding compound offering optimized cure characteristics and excellent electrical properties. Type ASTM 5948 CFG, and UL recognized under c.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 3554 Phenolic, Granular, Compression Molded PLENCO 03554 is an organic reinforced phenolic molding compound modified with PTFE to offer improved coefficient of friction values. 03554 is available in black. It is UL listed. 03554 is a re-numbe.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 4599 Phenolic, Granular, Injection Molded PLENCO 04599 is a mineral filled, phenolic molding compound offering excellent heat resistance and dimensional stability, typically required for automotive ashtray applications. 04599 is formulated .. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 6582 Phenolic, Briquette, Injection Molded PLENCO 06582 is a rubber modified phenolic molding compound, offering excellent heat resistant properties, along with improved mechanical strength at elevated temperatures. UL recognized under compo.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 6990 Phenolic, Briquette, Transfer Molded PLENCO 06990 is a glass and mineral filled novolac phenolic molding compound. UL recognized under component file E40654.Information supplied by Plenco. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 7591 Phenolic, Briquette, Injection Molded PLENCO 07591 is a mineral and flock cotton filled novolac phenolic molding compound. UL recognized under component file E40654.Information supplied by Plenco. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ISO 527 |
Wellman Wellamid® 22LHI4 XE-N Impact Modified Nylon 66, Lubricated & Heat Stabilized Typical Applications: Automotive fasteners, living hinge, head lamp adjustment devices, ink pen components, wire separators, hardware components, window installation clips, safety equipment.Data pro.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ISO 37 |
Lubrizol ESTANE® GP52DB Ester Based Thermoplastic Polyurethane Type: Estane® GP 52DB is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsAvailable in EuropeInformation provided b.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 4301 Phenolic, Granular, Compression Molded PLENCO 04301 is a heat resistant, mineral filled phenolic molding compound offering excellent dimensional stability and electrical properties. UL recognized under component file E40654. 04301 is ava.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ISO 527-1, 2 |
Polyplastics Duranex® 407EP Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ISO 527 |
Eastman Eastar AN004 Natural PCTA Copolyester EASTAR AN004 Copolyester contains a mold release. It has excellent appearance and is nearly water-clear. Its most outstanding features are its chemical resistance and processing capabilities. Exp.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Covestro Bayblend® FR 110 Polycarbonate/ABS Blend Flame retardant grade with antimony, chlorine and bromine free, flame retardant package, good light stability.Applications: Housings for business machines.Information provided by Bayer.As of 1 Septe.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Covestro Makrolon® T 7435 Polycarbonate, High Impact Impact modified injection molding grade, extremely easy flow and easy mold release, housings for portable mobile phones.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience wa.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ISO R527 |
Arkema Group Orgalloy® LE 60 SF Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ISO R527 |
Arkema Group Orgalloy® LE60 THM Polyamide Alloy Polyamide Alloy, Semi-Flexible gradeTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 102 Polypropylene, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plaskolite West Optix® CA-51 General Purpose Acrylic Resin Injection Molding and Extrusion Grade Pellets. Medium heat resistance and medium flow. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plenco 4311 Phenolic, Granular, Transfer Molded PLENCO 04311 is a heat resistant, mineral filled phenolic molding compound offering excellent processability, mechanical strength, and improved cold powder pourability characteristics. UL recognized.. |
|||
Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
Plaslok 308 Black (INJ) Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 308 is a two-stage, mineral and flock.. |