LG Chemical Lupoy 1603-06 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupoy 1603-06 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: LUPOY PC 1603-06 resin is designed for extrusion products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Characteristics: UV Stabilizer, High viscosity, Good mold release and High melt strengthApplications: Structure sheets and Multi-wall sheetsCAS: 103598-77-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.32 % @Temperature 23.0 °C |
0.32 % @Temperature 73.4 °F |
equilibrium, 50% RH; ASTM D570 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.00070 cm/cm | 0.00050 - 0.00070 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ASTM D638 |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ASTM D638 |
| Flexural Yield Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| Izod Impact, Notched | 9.074 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
17.00 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
0.25 mm notch; ASTM D256 |
| Izod Impact, Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 68.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C @Thickness 4.00 mm |
259 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| Vicat Softening Point | 180 °C @Load 5.10 kg |
356 °F @Load 11.2 lb |
50°C/hr; ASTM D1525 |
| Softening Point | 150 - 200 °C | 302 - 392 °F | melting point per MSDS |
| Flash Point | >= 450 °C | >= 842 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542 |
| Haze | 0.70 - 1.5 % | 0.70 - 1.5 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Autoignition Temperature | >450°C |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C1200HF PC+ABS (Asia Pacific)
- Polymer Resources PPX-GP3 Modified-PPO, General Purpose
- DuPont Bynel® 4206 Anhydride-Modified LDPE Adhesive Resin
- Zhejiang Juner JEPPB006 High Glossy PP
- ExxonMobil LLDPE LL 1236.86 Linear Low Density Polyethylene Resin
- Arlon Thermabond® R36300W008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- BASF Ultramid® 82335G HS BK 102 50% Glass Filled PA6 (Conditioned)
- 3M Novec™ Contact Cleaner Plus
- Solvay Specialty Polymers Algoflon® A.15 PTFE (Polytetrafluoroethylene) (discontinued **)