Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D651 |
Resinoid 1363 Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance |
|||
Tensile Strength, Ultimate | 50.0 - 130 MPa @Temperature 125 - 275 °C |
7250 - 18900 psi @Temperature 257 - 527 °F |
Average value: 86.7 MPa Grade Count:1 |
Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled". Each property range of values reported i.. |
|||
Tensile Strength, Ultimate | 50.0 - 120 MPa | 7250 - 17400 psi | Average value: 90.1 MPa Grade Count:8 |
Overview of materials for Polystyrene + Polyphenylene Ether, Glass + Mineral Filler This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene + Polyphenylene Ether, Glass + Mineral Filler". Each property range of values reported is mi.. |
|||
Tensile Strength, Ultimate | 50.0 MPa @Temperature 120 °C |
7250 psi @Temperature 248 °F |
ISO 527 |
LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
Tensile Strength, Ultimate | 50.0 - 123 MPa | 7250 - 17900 psi | Average value: 91.5 MPa Grade Count:11 |
Overview of materials for ABS/Polyester Alloy + GF This property data is a summary of similar materials in the MatWeb database for the category "ABS/Polyester Alloy + GF". Each property range of values reported is minimum and maximum values of appro.. |
|||
Tensile Strength, Ultimate | 50.0 - 2100 MPa | 7250 - 305000 psi | Average value: 760 MPa Grade Count:22 |
Overview of materials for Epoxy/Carbon Fiber Composite This property data is a summary of similar materials in the MatWeb database for the category "Epoxy/Carbon Fiber Composite". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Strength, Ultimate | 50.0 - 58.0 MPa | 7250 - 8410 psi | Average value: 55.3 MPa Grade Count:3 |
Overview of materials for Phenolic, Resole, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Resole, Mineral Filled". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Ultimate | 50.0 - 265 MPa | 7250 - 38400 psi | Average value: 187 MPa Grade Count:44 |
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl.. |
|||
Tensile Strength, Ultimate | 50.0 - 140 MPa | 7250 - 20300 psi | Average value: 72.5 MPa Grade Count:4 |
Overview of materials for Nylon, Amorphous Transparent Alloy This property data is a summary of similar materials in the MatWeb database for the category "Nylon, Amorphous Transparent Alloy". Each property range of values reported is minimum and maximum value.. |
|||
Tensile Strength, Ultimate | 50.0 MPa @Temperature 22.0 °C |
7250 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 0500 Unsaturated Polyester UP SMC 0500 is a special SMC with reduced density. The glass level has been selected to combine good moulding with good strength and stiffness properties. Even without a specific fire retardant the fir.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
Lucite International Perspexâ„¢ XT IM60 Acrylic Impact Modified Extruded Sheet PERSPEX extruded sheet has a lower molecular weight making it easy to vacuum form and the extrusion process gives excellent thickness tolerance and is economical for long production runs.Information.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Plenco 3356 Phenolic, Granular, Compression Molded PLENCO 03356 is a mineral filled phenolic molding compound offering excellent arc resistance, comparative tracking, and flame resistant properties. UL recognized under component file E40654. 03356 i.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Plenco 3557 Phenolic, Granular, Compression Molded PLENCO 03557 is a woodflour and mineral filled phenolic molding compound offering excellent dielectric strength values at elevated temperatures while maintaining mechanical strength properties. UL r.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Tipco Tipcolite® TG 211 Phenolic Compound, Mineral & Wood Flour, Soft Flow & High Electrical Properties Soft Flow Phenolic Compound, Reinforced with Mineral & Wood FlourApplications: Electrical & ElectronicsProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Tipco Tipcolite® THD 321 Phenolic Compound, Wood Flour & Cellulose, having Soft Flow & High Strength Soft Flow Phenolic Compound, Reinforced with Wood Flour & CelluloseApplications: Switchgear, HRC FusesProcessing: Compression & TransferInformation provided by the Manufacturer, Tipco Industries Lt.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Tipco Tipcolite® TMHS 291 Phenolic Compound, Khaki Cotton Fabric, in fluffy form, Soft Flow & High Impact Strength Soft Flow Phenolic Compound, Reinforced with Khakhi Cotton Fabric, in fluffy formApplications: Defence ApplicationsProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Ind.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ISO 527-1, 2 |
Polyplastics Duracon® SW-01 Acetal Co-polymer (POM), High sliding, Special lubricant, High sliding DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | DIN 53504 |
Lubrizol ESTANE® 5701F1 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | |
Covestro Baydur® 110 FR Polyurethane Rigid microcellular RIM polyurethane material. Fast demold times; self releasing; long flow paths possible, therefore suitable for production of large moldings. Parts are injected through only one .. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | cond; ISO 527-1/-2 |
DSM Akulon® K224-PG2 PA6-I-GF8 8% Glass Reinforced, Impact Modified |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ISO R527 |
Arkema Group Orgalloy® LE 60 LM Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ATSM D638 |
Ashley Polymers Ashlene® ABS Resin F-214 General purpose, medium impact resin.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 50.0 - 60.0 MPa | 7250 - 8700 psi | ASTM D638 |
Chang Chun Plastic PBT1200M General Purpose PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 420 Polyester - PBT, Glass/Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ATSM D638 |
Ashley Polymers Ashlene® PPO Resin P257 A high flow grade for applications requiring high impact strength, heat resistance and dimensional stability.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 50.0 - 90.0 MPa | 7250 - 13100 psi | Average value: 73.5 MPa Grade Count:7 |
Overview of materials for Nylon 66, Nucleated This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Nucleated". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Tensile Strength, Ultimate | 50.0 - 80.0 MPa @Temperature 160 - 160 °C |
7250 - 11600 psi @Temperature 320 - 320 °F |
Average value: 70.2 MPa Grade Count:1 |
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% .. |
|||
Tensile Strength, Ultimate | 49.99 MPa | 7250 psi | |
Phenolic 46%, Carbon fabric 54% Phenolic - Monsanto "SC 1008". Carbon fabric - "VCA" |
|||
Tensile Strength, Ultimate | 50.0 - 170 MPa @Temperature -40.0 - 120 °C |
7250 - 24700 psi @Temperature -40.0 - 248 °F |
Average value: 83.0 MPa Grade Count:2 |
Overview of materials for Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant". Each property range of values re.. |
|||
Tensile Strength, Ultimate | 50.0 - 103 MPa | 7250 - 15000 psi | Average value: 69.7 MPa Grade Count:7 |
Overview of materials for Polybutylene Terephthalate (PBT), Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Aramid Fiber Filled". Each property range of values reported is minimu.. |