DSM Akulon® K224-PG2 PA6-I-GF8
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Akulon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Akulon® K224-PG2 PA6-I-GF8.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
8% Glass Reinforced, Impact Modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | dry; ISO 1183 |
| Water Absorption | 7.6 % | 7.6 % | Sim. To ISO 62 |
| Moisture Absorption | 2.20 % | 2.20 % | Sim. To ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | cond; ISO 527-1/-2 |
| 85.0 MPa | 12300 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 5.5 % | 5.5 % | dry; ISO 527-1/-2 |
| 15 % | 15 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 1.90 GPa | 276 ksi | cond; ISO 527-1/-2 |
| 3.70 GPa | 537 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eU |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 2.20 J/cm² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | dry; ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
dry; IEC 60695-11-10 |
Users viewing this material also viewed the following:
- Resinlab® AR 4400 Metal & Composite Bonding Methacrylate Adhesive
- Karina TR-500D10/1-YV White PVC Compound
- CP-Polymer-Technik Wellamid® 6600 GS 15 HWCP 15% Glass Sphere Filled Nylon 66, Heat Stabilized, Conditioned
- ExxonMobil Jayflex™ DIDP Plasticizer
- Eurotec® Tecomid® NA40 GR30 NL RM PA6.6, 30% glass fiber reinforced, MoS2 modified, natural
- BASF Elastollan SP 9213 TPUR
- A. Schulman SCHULAMID® 66 GB40 40% Glass Bead Reinforced Nylon 66
- Plenco 50240 PET, Pellet, Injection Molded, Black (discontinued **)
- Plaslok 501 Black Electrical Grade Mineral/Flock Filled Phenolic Molding Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved