Arkema Group Orgalloy® LE 60 LM Polyamide Alloy
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® LE 60 LM Polyamide Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Film and PackagingInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO R1183 |
| Water Absorption | 0.80 % | 0.80 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 23°C / 50% RH; ISO 62 |
| 6.4 % | 6.4 % | in 23°C water; ISO 62 | |
| Melt Flow | 1.2 g/10 min @Load 2.16 kg, Temperature 235 °C |
1.2 g/10 min @Load 4.76 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ISO R527 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO R527 |
| Elongation at Break | >= 250 % | >= 250 % | ISO R527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO R527 |
| Modulus of Elasticity | 0.700 GPa | 102 ksi | ISO R527 |
| Flexural Strength | 28.0 MPa | 4060 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| Flexural Modulus | 0.650 GPa | 94.3 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| Charpy Impact, Notched | 32.0 J/cm² @Temperature -20.0 °C |
152 ft-lb/in² @Temperature -4.00 °F |
After conditioning at 23°C/50%RH; ISO 179/Af |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/Af |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced
- Imerys 325FFâ„¢ Ground Mica
- H.C. Starck Amperit® 588.059 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr)
- Stellarchem MP-860Q TPE Compound
- Dow Corning Q7-9120 Silicone Fluid, 100 CST
- Eurotec® Tecodur® PB70 GR23 BK EF PBT, 23% glass fiber reinforced, black, suitable for electrostatic powder coating, gas injection grade
- Addiplast Addilene H 560 Polypropylene Homopolymer
- BASF Neopolen® P 9335 MG 0.035 g/cc Core density; Expanded Polypropylene (Europe)
- Barlog Plastics KEBAFLEX S 70 A.01 TPE-S, Shore A70, translucent
- Aremco Ceramabond™ 890 High Temperature Ceramic Adhesive/Paste, Silicon Carbide Filled
Copyright © lookpolymers.com All Rights Reserved