Chang Chun Plastic PBT1200M General Purpose PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Chang Chun Plastic Co. Ltd. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chang Chun Plastic PBT1200M General Purpose PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Dowell Trading Company Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 - 1.32 g/cc | 0.0470 - 0.0477 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0080 - 0.020 cm/cm | 0.0080 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 - 90 | 85 - 90 | ASTM D785 |
| Tensile Strength, Ultimate | 50.0 - 60.0 MPa | 7250 - 8700 psi | ASTM D638 |
| Elongation at Break | 50 - 90 % | 50 - 90 % | ASTM D638 |
| Flexural Yield Strength | 75.0 - 85.0 MPa | 10900 - 12300 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 0.440 - 0.540 J/cm @Thickness 6.35 mm |
0.824 - 1.01 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 225 °C | 437 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/32 in. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 60 Hz |
3.3 @Frequency 60 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60 Hz |
0.0010 @Frequency 60 Hz |
ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Plastcom PLASTALEN® PQ 81 T 20 Polypropylene reinforced with mineral filler, impact modified
- Nabaltec NABALOX® NO 615-30 Reactive Alumina
- SABIC Innovative Plastics Lexan® 123R PC (Asia Pacific)
- SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC
- Lucas-Milhaupt Silvabrite® 100® Lead-Free Solder
- Solvay TECHNYL® A 50H1 PA66, Conditioned
- Techmer ES HiFill® PA6/6 GF60 IM HS L 60% Glass Filled (Conditioned)
- SABIC Innovative Plastics LNP THERMOTUF RF008IS PA 66 (Asia Pacific)
- ExxonMobil Mobil Zerice 32 S Oil
- DuPont Bynel® 3933 Anhydride-Modified Ethylene Vinyl Acetate Adhesive Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved