- Polymer Property : Tensile Strength, Ultimate = 3630 psi
Polymer Property : Tensile Strength, Ultimate = 3630 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| NCMT NanoPAC™ N12 High Performance Polypropylene Nanocomposite Characteristics: Less shrinkage Solved distortion problem Good balance in impact and stiffness High gloss Reduce production cycleApplications: Household Industry Toys IndustryInformation provided by.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| North Wood Plastics Polypropylene with 20% Wood Fiber, Molding Grade Data provided by North Wood Plastics, Inc. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| North Wood Plastics Polypropylene with 40% Wood Fiber, Molding Grade Data provided by North Wood Plastics, Inc. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| Total Finaclear® 530 Clear Impact Polystyrene
(discontinued **) Finaclear® 530 is a clear high styrenic styrene-butadiene (SBS) elastomer, providing dramatically improved impact properties and tear resistance to finished articles, when used in blends with other.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | DIN 53455 |
| Ineos Nova S-3401 Medium Impact Compact Polystyrene
(discontinued **) Impact polystyrene with good flow characteristics and a high elongation. Generally used for applications where a tough material is required. The material is provided with external lubricate to imp.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | DIN 53455 |
| Ineos Nova S-6600 High Impact Compact Polystyrene
(discontinued **) High impact polystyrene which is very easy processed in extension and thermoforming processes. Typical applications are packaging of food stuffs like Yot beakers but technical parts and extruded pr.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | DIN 53455 |
| Ineos Nova S-6600MG Compact Polystyrene Microgranulates
(discontinued **) High impact polystyrene Microgranulates, having a diameter of 0.8 - 1.0 mm especially useful for compounding and extrusion applications. Due to the higher viscosity intensive mixing with thermoplas.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | 500 mm/min (20 in./min.); Type IV Specimen; ASTM D638 |
| Eastman M2001-P Polyethylene
(discontinued **) M2001-P polyethylene is suggested for applications such as spiral-wound can linings, release paper and photographic paper. M2001-P has been found to exhibit good barrier properties, temperature res.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
| Eastman M2004-P Polyethylene
(discontinued **) M2004-P polyethylene is suggested for applications such as spiral-wound can linings, release paper and photographic paper. M2004-P has been found to exhibit good barrier properties, temperature res.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| ExxonMobil Iotek® 7010 Zinc Ionomer Molding/Extrusion Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A zinc ionomer with excellent flexibility, abrasion resistance, impact strength and tensile strength. This ionomer has outstanding adhesion to glas.. |
|||
| Tensile Strength, Ultimate | 25.0 - 75.5 MPa | 3630 - 11000 psi | Average value: 39.2 MPa Grade Count:34 |
| Overview of materials for Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded". Each property range of values reported is m.. |
|||
| Tensile Strength, Ultimate | 25.0 - 178 MPa @Temperature -40.0 - 150 °C |
3630 - 25800 psi @Temperature -40.0 - 302 °F |
Average value: 66.1 MPa Grade Count:9 |
| Overview of materials for Nylon 6, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |
|||
| Tensile Strength, Ultimate | 25.0 - 145 MPa @Temperature -30.0 - 120 °C |
3630 - 21000 psi @Temperature -22.0 - 248 °F |
Average value: 66.1 MPa Grade Count:1 |
| Overview of materials for Nylon 6, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |
|||
| Tensile Strength, Ultimate | 25.0 - 215 MPa @Temperature -40.0 - 150 °C |
3630 - 31200 psi @Temperature -40.0 - 302 °F |
Average value: 88.6 MPa Grade Count:5 |
| Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
| Tensile Strength, Ultimate | 25.0 - 400 MPa @Temperature -40.0 - 200 °C |
3630 - 58000 psi @Temperature -40.0 - 392 °F |
Average value: 101 MPa Grade Count:5 |
| Overview of materials for Nylon 66, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. .. |
|||
| Tensile Strength, Ultimate | 25.0 MPa @Temperature 22.0 °C |
3630 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Menzolit Menzolit® BMC 2600 Unsaturated Polyester UP BMC 2600 is a special BMC with reduced electrical properties. The glass content is set to a level that combines good mouldability with good strength and stiffness properties. Because of its improved.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 394 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 25.0 - 35.0 MPa | 3630 - 5080 psi | ASTM D638 |
| Zeus PFA Tubing PFA, or perfluoroalkoxy, is well recognized for its ability to maintain mechanical integrity in extreme temperatures even when exposed to caustic chemicals. PFA comes in high purity versions that ar.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa @Temperature 80.0 °C |
3630 psi @Temperature 176 °F |
ASTM D638 |
| Toyobo NB-5620S Nylon/Olefin Alloy, 15% Mineral Reinforced (DAM) Features: 15% Mineral Reinforced, Light WeightInformation provided by Toyobo. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 394 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 394 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ISO 527-1/-2 |
| DSM Arnitel® EM400-BP TPC-ET 34 Shore D, Injection Molding or Extrusion Grade |
|||
| Tensile Strength, Ultimate | 25.0 - 40.0 MPa | 3630 - 5800 psi | |
| Alliance BIN-48 Bonded (Composite) Magnetic Material |
|||
| Tensile Strength, Ultimate | 25.0 - 40.0 MPa | 3630 - 5800 psi | |
| Alliance BIN-55 Bonded (Composite) Magnetic Material |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| A. Schulman ComAlloy Comtuf® 164 Polypropylene, Mineral Reinforced, Chemically Coupled, Impact Modified Data provided by the manufacturer, ComAlloy International Company.20% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i.. |
|||
| Tensile Strength, Ultimate | 25.0 - 215 MPa @Temperature -55.0 - 275 °C |
3630 - 31200 psi @Temperature -67.0 - 527 °F |
Average value: 109 MPa Grade Count:18 |
| Overview of materials for Polyetheretherketone, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Glass Fiber Filled". Each property range of values reported is minimum and maximum.. |
|||
| Tensile Strength, Ultimate | 25.0 - 325 MPa | 3630 - 47100 psi | Average value: 114 MPa Grade Count:222 |
| Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
| Tensile Strength, Ultimate | >= 25.0 MPa | >= 3630 psi | ASTM D638 |
| Borealis Borstar® HE6062 HDPE Black Jacketing Compound Borstar HE6062 is a black, bimodal co-polymer high density polyethylene (HDPE) compound produced using the Borealis Borstar process. It is characterized by balanced properties important in jacketin.. |
|||