- North Wood Plastics Polypropylene with 40% Wood Fiber, Molding Grade
North Wood Plastics Polypropylene with 40% Wood Fiber, Molding Grade
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Wood Filled |
| Manufacturer | North Wood Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | North Wood Plastics Polypropylene with 40% Wood Fiber, Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by North Wood Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.039 g/cc | 0.03754 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Melt Flow | 2.4 g/10 min @Temperature 190 °C |
2.4 g/10 min @Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 5.4 % | 5.4 % | ASTM D638 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ASTM D638 |
| Flexural Yield Strength | 48.0 MPa | 6960 psi | ASTM D790 |
| Flexural Modulus | 3.30 GPa | 479 ksi | 1% Secant at 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.220 J/cm | 0.412 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.840 J/cm | 1.57 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C @Temperature 20.0 °C |
27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 200 °C | <= 392 °F | To prevent fiber degradation. |
Users viewing this material also viewed the following:
- PolyOne Aquamix™ 142 Latex
- SABIC Innovative Plastics LNP LUBRICOMP AL004 ABS (Asia Pacific)
- Imerys Bardenâ„¢ R Kaolin
- Samsung Cheil Industries Starex® NH-1907 HIPS, Unreinforced FR
- SABIC Innovative Plastics LNP THERMOCOMP VC006 SUPER TOUGH NYLON
- A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer
- Covestro Bayblend® FR 3010 Polycarbonate + ABS, Flame Retardant Grade
- C.O.I.M. EXTER S® S 110 Orthophthalic Resin
- BASF Ultramid® KR 4355 G10 BK 23215 50% Glass Filled PA6/6T (Dry)
- A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved