Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 18.8 MPa | 2730 psi | ASTM D412-80 |
DuPont Performance Polymers Hypalon® 45 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound
(discon Mineral filled compound with 100 parts Hypalon; 80 parts hard clay; 4 parts magnesia; 30 parts aromatic process oil; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont .. |
|||
Tensile Strength, Ultimate | 18.8 MPa | 2730 psi | Cured |
KKPC KOSYN KBR 31 Polybutadiene Rubber (High cis BR) Polybutadiene Rubber (High cis BR)Characteristics: KBR 31 contains an aromatic oil additive. Polybutadiene Rubber (BR), which has three kinds of bond structure of cis-1,4, trans-1,4, vinyl, is simp.. |
|||
Tensile Strength, Ultimate | 18.8 MPa | 2730 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4520 Molded Brake Part FormulationNordel® IP 4520 |
|||
Tensile Strength, Ultimate | 18.8 MPa | 2730 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4770P General Purpose Compound FormulationNordel® IP 4770P |
|||
Tensile Strength, Ultimate | 18.8 MPa | 2730 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4770R General Purpose Compound FormulationNordel® IP 4770R |
|||
Tensile Strength, Ultimate | 18.8 - 152 MPa | 2730 - 22000 psi | Average value: 42.9 MPa Grade Count:18 |
Overview of materials for Polypropylene, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Film Grade". Each property range of values reported is minimum and maximum values of appr.. |