Polymer Property : Tensile Strength, Ultimate = 20000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	138 MPa	20000 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® PK-15CF-15GB/000 Polyetheretherketone (PEEK), Glass Bead, Carbon Fiber Reinforced (discontin Description/Features:Carbon Fiber ReinforcedGlass Bead FilledPolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate	138 MPa	20000 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Lubri-Tech™ PF-30CF/15T Polysulfone, Carbon Fiber Reinforced, PTFE Lubricated (discontinued **) Description/Features:Carbon Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate	138 MPa	20000 psi	ASTM D638
Global GPC-140 40% Glass Filled Polycarbonate Information provided by Global Polymers Corporation.
Tensile Strength, Ultimate	138 MPa	20000 psi
Meehanite GF-20 Flake Graphite Cast Iron Type GF-20 is designed principally for high machinability and is used where ultimate strength is not an important factor.General Meehanite information - Meehanite metal is first melted to a definite..
Tensile Strength, Ultimate	138 MPa	20000 psi
MTI ThermoStranÂ® PP-30C Long Carbon Fiber Compound ThermoStranÂ® is custom designed long fiber thermoplastic compound (LFC) engineered to meet specific end use requirements. Continuous fibers are pultruded to yield pellets with fibers equivalent t..
Tensile Strength, Ultimate	138 MPa	20000 psi	ASTM D638
Techmer ES ElectrafilÂ® J-1/CF/10 Nylon 66, 10% Carbon Fiber Reinforced
Tensile Strength, Ultimate	138 MPa	20000 psi	ASTM D638
Techmer ES PlaslubeÂ® J-4/30/TF/15 Nylon 612, 30% GFR, 15% PTFE Plaslube glass fiber reinforced polytetrafluoroethylene (PTFE) lubricated nylon 612 grades offer a unique balance of excellent wear and friction performance with good dimensional stability and mecha..
Tensile Strength, Ultimate	138 MPa	20000 psi	ASTM D638
Sumitomo Bakelite SumikonÂ® PM-9640 Glass Filled Phenolic Two stage glass fiber filled black phenolic. It is especially designed for applications requiring high strength and dimensional stability with excellent heat resistance. PM-9640 is widely used in ..
Tensile Strength, Ultimate	138 MPa	20000 psi	ACMA Test #4
CeramTec 771 94% Alumina (Al2O3) Te value is 840°C. Hasselman Thermal Shock value is 200 K.Data provided by CeramTec North America.
Tensile Strength, Ultimate	138 - 207 MPa	20000 - 30000 psi
Cosmic Plastics CP7311 Epoxy Molding Compound Data provided by the manufacturer.
Tensile Strength, Ultimate	138 MPa	20000 psi	ISO 527-1, 2
Polyplastics Duranex® CN5330 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 30% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate	138 MPa	20000 psi	annealed
CMW® ELKONIUM 30 pure platinum Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (..
Tensile Strength, Ultimate	138 MPa	20000 psi	5 mm/min
Arkema Group Rilsan® AZM 43 G9 T6LD Nylon 12, 43% Glass Fiber Filled (Dry) Designation ISO 1874-PA12,MHLS,16-080,(G+C)(F+D)(43+05)Rigid grade with glass fiber (43%) and graphite filler for injection molding. Available color: steel black gray. Reinforced light and heat stab..
Tensile Strength, Ultimate	138 MPa	20000 psi	ASTM D638
Adell AL-18 Nylon 66, 40% Glass Reinforced; Mineral Filled Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate	138 MPa	20000 psi	ASTM D638
Chem Polymer Chemlon 109-33 G Nylon 66, 33% Glass Fiber Reinforced A highly toughened 33% glass fiber reinforced nylon 66 developed for applications requiring stiffness, creep resistance and impact resistance.Data provided by the manufacturer, Chem Polymer.
Tensile Strength, Ultimate	138 MPa	20000 psi	ASTM D638
A. Schulman ComAlloy Hiloy® 516 Polycarbonate, Carbon Fiber Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	138 MPa	20000 psi	ASTM D638
Adell ZR-37 33% Glass Reinforced Nylon/Olefin Alloy Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate	138 MPa @Temperature 871 °C	20000 psi @Temperature 1600 °F
Carpenter Gall-Tough® Stainless Data provided by Carpenter Technology Corporation.6.4 mm diameter tensile specimens from center of 25.4 mm diameter bar annealed 1066°C 1 hour, water quenched, and ground.Threshold Galling Stress 1..
Tensile Strength, Ultimate	138 MPa	20000 psi	ATSM D638
Ashley Polymers Ashlene® ABS Resin F-217 General purpose super high impact with good gloss.Data provided by the manufacturer
Tensile Strength, Ultimate	138 MPa	20000 psi	ISO value at 5mm/min.
BASF Capron® 8334G Impact Modified, 40% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron 8334G is a heat stabilized, 40% glass fiber reinforced polyamide 6 molding compound developed for applications requiring a high level of stiffness combined with excellent impact performance. ..
Tensile Strength, Ultimate	138 MPa	20000 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® PI-10CF/000 Polyetherimide (PEI), Carbon Fiber Reinforced (discontinued **) Description/Features:Carbon Fiber ReinforcedElectrically ConductiveInformation provided by PolyOne Corporation.