- Techmer ES Electrafil® J-1/CF/10 Nylon 66, 10% Carbon Fiber Reinforced
Techmer ES Electrafil® J-1/CF/10 Nylon 66, 10% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | Electrafil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Electrafil® J-1/CF/10 Nylon 66, 10% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 52 | 52 | ASTM D785 |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 7.58 GPa | 1100 ksi | ASTM D638 |
| Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Compressive Strength | 124 MPa | 18000 psi | ASTM D695 |
| Shear Strength | 68.9 MPa | 10000 psi | ASTM D732 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm |
0.800 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 4.27 J/cm @Thickness 3.17 mm |
8.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 27.0 µm/m-°C @Temperature 20.0 °C |
15.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 100 - 1000 ohm-cm | 100 - 1000 ohm-cm | ASTM C611 |
| Surface Resistance | 10000 ohm - 1e+05 | 10000 ohm - 1e+05 | ASTM D4496 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® ML7667 PC Copolymer (Europe-Africa-Middle East)
- Hyosung Topilene J700-1 PP
- Stellar Canada CERAMITE® CSR Wear Resistant Castable
- SABIC Innovative Plastics LNP STAT-LOY N30009 PC+ABS (Asia Pacific)
- Tisan TISLAMID® 66 15% Mineral Filled Flame Retardant (V0). Heat Stabilized Nylon 66
- DSM Stanyl® TW441 Nylon 46 (European and Asian Grade) (Cond)
- ACC EP RAP 60 EPI Engineered Polymers Aliphatic Polyurea
- SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS (Asia Pacific)
- CENTROPLAST CENTROLEN PP LF Polypropylene conductive
Copyright © lookpolymers.com All Rights Reserved