CeramTec 771 94% Alumina (Al2O3)
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | CeramTec North America |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CeramTec 771 94% Alumina (Al2O3).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Te value is 840°C. Hasselman Thermal Shock value is 200 K.Data provided by CeramTec North America.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.60 g/cc | 0.130 lb/in³ | |
| Water Absorption | 0.00 % | 0.00 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Vickers Microhardness | 1200 | 1200 | HV 0.5 |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | ACMA Test #4 |
| Modulus of Elasticity | 281 GPa | 40800 ksi | Ultrasonic |
| Flexural Strength | 262 MPa | 38000 psi | 20 x 40 mm |
| Compressive Strength | 1931 MPa | 280100 psi | ASTM C773-88 |
| Poissons Ratio | 0.24 | 0.24 | ASTM C-1 259-94 |
| Fracture Toughness | 2.70 MPa-m½ | 2.46 ksi-in½ | |
| Shear Modulus | 113 GPa | 16400 ksi | Ultrasonic |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 6.00 µm/m-°C @Temperature 25.0 - 300 °C |
3.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
| 7.20 µm/m-°C @Temperature 25.0 - 700 °C |
4.00 µin/in-°F @Temperature 77.0 - 1290 °F |
||
| 7.40 µm/m-°C @Temperature 25.0 - 1001 °C |
4.11 µin/in-°F @Temperature 77.0 - 1834 °F |
||
| Specific Heat Capacity | 0.900 J/g-°C | 0.215 BTU/lb-°F | |
| Thermal Conductivity | 27.7 W/m-K | 192 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 1500 °C | 2730 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 7.00e+6 ohm-cm @Temperature 700 °C |
7.00e+6 ohm-cm @Temperature 1290 °F |
|
| >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
||
| Dielectric Constant | 8.9 @Frequency 1e+6 Hz |
8.9 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 8.268 kV/mm @Thickness 6.35 mm |
210.0 kV/in @Thickness 0.250 in |
|
| Dissipation Factor | 0.00030 @Frequency 1e+6 Hz |
0.00030 @Frequency 1e+6 Hz |
|
| 0.0010 @Frequency 1e+10 Hz |
0.0010 @Frequency 1e+10 Hz |
||
| Dielectric Loss Index | 0.0027 | 0.0027 | 1 MHz; 20°C |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ A700 BK VN4255 LS Polyamide 66 (Nylon 66)
- Plastcom SLOVALEN PC 99 GF 30/1M Polypropylene reinforced with glass fiber, improved flowing
- Ineos Nova 2511 General Purpose Crystal Polystyrene (discontinued **)
- LG Chemical LUTENE-H XL1800 HDPE
- Solvay Specialty Polymers Algoflon® L105 Polytetrafluoroethylene (PTFE)
- Saint-Gobain Chemlam® SGC6-04 Copper Adhesive Tape
- A. Schulman FORMION™ FI 232 10% Mineral Reinforced Ionomer / Nylon Alloy
- Chosun Refractories TCH-175SV Torpedo Castable
- ATI Allegheny Ludlum Stainless Steel AL 904L™ Alloy (UNS N08904)
Copyright © lookpolymers.com All Rights Reserved