Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ISO 527 |
LATI LAESTRA E01 G/30 30% Glass Fiber Reinforced, Elastomer Modified Syndiotactic Polystyrene (SPS)
(disconti Description: Laestra compounds are syndiotactic polystyrene (SPS) products. SPS is a polymer offering a combination of properties unavailable with other materials. It exhibits a melting point of 270.. |
|||
Tensile Strength, Ultimate | 110 - 159 MPa | 16000 - 23000 psi | Average value: 137 MPa Grade Count:14 |
Overview of materials for Polyetherimide (PEI), 20% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 20% Glass Fiber". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
IDI Composites E-206 Thermoset Polyester, Sheet ELECTRICAL - U.L. recognized (E53587). Versatile family of compounds designed to meet the most demanding electrical and electronic applications. Excellent dielectric properties and arc/track resista.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | |
Haysite H258 Polyester Laminate Solder Pallet and Work Holder Sheet A high temperature polyester laminate that exhibits excellent retention of mechanical properties and dimensional stability at elevated temperatures. Applications.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | |
Haysite H260 Polyester Laminate Solder Pallet and Work Holder Sheet An advanced composite that is high temperature resistant and high strength with semi-conductive properties. Engineered for use as wave and reflow solder pallet m.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
Techmer ES Plaslube® J-50/20/SI/2 Polycarbonate, 20% GFR, 2% Silicone |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ISO 527-1, 2 |
Polyplastics Duranex® 313RA Polybutylene Terephthalate (PBT), Resin adhesion improved for multiple injection molding, 15% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM-D638 |
Toyobo VYLOPET® EMC320R Polyester Resin VYLOPET® is a polyester resin developed specifically for injection molding. Polyester resins have excellent heat resistance, rigidity, chemical resistance, and electric properties. Grade EMC320R ha.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
UBE UPIMOL® SA101 Heat-Resistant Polyimide Shape Description: UPIMOL® SA101 is an excellent heat-resistant polyimide shape, based on Biphenyl tetracarboxilic dianhydride(BPDA) originally developed by UBE. UPIMOL® SA101 has improved high durabili.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
DSM Akulon® Ultraflow K-FPG8 PA6-I-GF40 Glass Reinforced, High flow |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
DSM Stanyl® 46SF5030 PA46-GF30 FR(17) 30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
DSM Stanyl® TS241B3 PA46-CF15 15% Carbon Reinforced, Lubricated |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | |
Cytec Thornel® VCK Carbon Cloth Laminate with Mil R-9299 Resin Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | |
Cytec Thornel® VCK Carbon Fiber Cloth Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | |
Cytec Thornel® VCL Carbon Cloth Laminate with Mil R-9299 Resin Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | |
Cytec Thornel® VCL Carbon Fiber Cloth Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature.. |
|||
Tensile Strength, Ultimate | 110 - 140 MPa | 16000 - 20300 psi | ASTM D638 |
Chang Chun Plastic PBT4830 Fire Retardant & 30% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
Chem Polymer Chemlon 115 G Nylon 66, 15% Glass Fiber Reinforced A 15% glass fiber reinforced nylon 66 offering improved creep resistance, stiffness, tensile strength and dimensional stability over unmodified nylon 66 materials. This product offers slight improv.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 446 Glass/Mineral Reinforced, PET Alloy Data provided by the manufacturer, ComAlloy International Company.35% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
Adell AJ-14 Nylon 66, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
Adell AJ-34 Nylon 66, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |