- Polymer Property : Tensile Strength, Ultimate = 145000 psi
Polymer Property : Tensile Strength, Ultimate = 145000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | |
| PSM Industries Pacific Sintered Metals Nickel Steel FN-255-S(HT) Powdered Metal Good impact resistant mechanical components, Good hardenability Equivalent MPIF Specification: FN-0208-130HTInformation Provided by Pacific Sintered Metals, a division of PSM Industries |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | Hot-Worked |
| Kinetics MIM F1537 (ASTM F1537) HIP and Heat Treat Most commonly used within the medical market on applications requiring these characteristics: Bio-compatibility Corrosion resistance High strength Nonmagnetic Wear resistance. Information prov.. |
|||
| Tensile Strength, Ultimate | 1000 - 1070 MPa | 145000 - 155000 psi | |
| Materion BrushCAST® 165CT Fine Grain Casting Alloy (Solution Annealed & Aged) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
| Tensile Strength, Ultimate | >= 1000 MPa | >= 145000 psi | |
| MetalTek MTEK CA20NW Cast UNS J91631 Martensitic Stainless Steel Information provided by MetalTek |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | |
| International Mold Steel Superplast® Stainless Plastic and Rubber Mold Steel Superplast Stainless is a prehardened, free-machining, stainless mold steel specially designed for plastic mold bases. It also provides improved performances compared to standard grades such as W1.2.. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | |
| Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | Tempered at 1075°F, 4hr |
| Latrobe Lescalloy® 15-5 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 15-5 VAC-ARC steel is a precipitation hardening martensitic stainless steel commonly considered to be a compositional modification of 17-4 with minimal delta ferrite. A wide range of mec.. |
|||
| Tensile Strength, Ultimate | >= 1000 MPa | >= 145000 psi | H1075 Condition - 580°C at 4 hr |
| Latrobe Lescalloy® 17-4 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150°F (482-621°C) tempe.. |
|||
| Tensile Strength, Ultimate | 998 MPa | 145000 psi | |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | |
| Kinetics MIM 17-4PH Stainless Steel (H1100 Condition) Precipitation-hardening stainless steel. Offers a good balance between corrosion resistance and strength. Magnetic. Hardenable to various strength levels and hardness by varying the aging heat treat.. |
|||
| Tensile Strength, Ultimate | 1000 - 1070 MPa | 145000 - 155000 psi | |
| Materion BrushCAST® 165C High Strength Casting Alloy (Solution Annealed & Aged) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
| Tensile Strength, Ultimate | >= 1000 MPa | >= 145000 psi | |
| MetalTek MTEK 535 Martensitic Stainless Steel Information provided by MetalTek |
|||
| Tensile Strength, Ultimate | 1000 MPa @Temperature 650 °C |
145000 psi @Temperature 1200 °F |
|
| Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Tensile Strength, Ultimate | 1000 - 1200 MPa | 145000 - 174000 psi | |
| SSAB Tunnplat Docol® 1000 DL High-strength Steel In course of development.Data provided by SSAB Tunnplat. |
|||
| Tensile Strength, Ultimate | 1000 - 1200 MPa | 145000 - 174000 psi | |
| SSAB Tunnplat Docol® 1000 DP High-strength Steel High-strength SteelCharacteristics: The steels are annealed at temperatures between 750°C and 850°C, depending on the grade of steel, and then are hardened by quenching in water. Tempering is.. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | Typical |
| TIMET TIMETAL® 1100 Titanium Alloy (Ti-6Al-2.7Sn-4Zr-0.4Mo-0.45Si) Features: A near alpha, high temperature creep resistant alloy developed for elevated temperature use in the range of 600°C that offers the highest combination of strength, creep resistance, fractu.. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | Typical |
| TIMET TIMETAL® 62S Titanium Alloy (Ti-6Al-2Fe-0.1Si); Annealed Sheet/Plate & Billet/Bar Low Cost, Multipurpose Alloy. Tensile property data below for Annealed Sheet/Plate & Billet/Bar.Features: Properties and processing characteristics equivalent to or better than TIMETAL 6-4, but wit.. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | Typical Transverse |
| TIMET TIMETAL® 62S Titanium Alloy (Ti-6Al-2Fe-0.1Si); Beta Forged Low Cost, Multipurpose Alloy. Tensile/toughness property data below for Beta Forged, RA material.Features: Properties and processing characteristics equivalent to or better than TIMETAL 6-4, but wi.. |
|||
| Tensile Strength, Ultimate | 1000 - 1200 MPa | 145000 - 174000 psi | as built |
| EOS MS1 Maraging Steel for DMLS 3D Printing EOS Maraging Steel MS1 is a steel powder which has been optimized especially for processing on EOSINT M 270 systems. This steel has very good mechanical properties, and is easily heat-treatable us.. |
|||
| Tensile Strength, Ultimate | 1000 - 1100 MPa | 145000 - 160000 psi | as built, Z direction |
| EOS PH1 Precipitation Hardening Stainless Steel for DMLS 3D Printing EOS Stainless Steel PH1 is a stainless steel powder which has been optimized especially for processing on EOSINT M 270 systems. This stainless steel prototyping material is tough and resistant to .. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | ASTM D3039 |
| Dow Fulcrum™ Thermoplastic Glass-Filled Polyurethane Composite Strip FULCRUM Thermoplastic Composite Technology is specifically designed for the fabrication of continuous fiber composites that have greater flexibility in post-processing operations as well as higher t.. |
|||
| Tensile Strength, Ultimate | 1000 - 1100 MPa | 145000 - 160000 psi | |
| CLAL-MSX NICLAFOR® 1000 TH4 Quenched/Cold Rolled/Precipitation Heat Treated, Rolled Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi.. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | cold worked |
| CMW® ELKONIUM 32 platinum based alloy Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (.. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | |
| Carpenter BioDur™ 316LS Stainless Medical Implant Alloy, 48% Cold Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Vacuum arc remelted (VAR), low carbon version of Type 316 stainless. The secondary premium melting step (VAR) imparts impro.. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | |
| ATI Allvac® Nickelvac® X-750 Nickel Superalloy, Heat Treatment: 1149°C (2100°F) + Age Data provided by Allvac.Applications: Turbine, engine components. Blades, vanes, fasteners, springs, bellows. Extrusion dies, nuclear, heat treating, forming tools. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | Typical |
| TIMET TIMETAL® 6-2-4-2 (Ti-6Al-2Sn-4Zr-2Mo-0.08Si) Titanium Alloy Medium-Strength, Elevated Temperature AlloyIndustry Specifications: USA Aerospace: AMS 4919.Features: TIMETAL 6-2-4-2 has good tensile creep and fatigue properties up to 540°C. It is the most comm.. |
|||
| Tensile Strength, Ultimate | 1000 MPa | 145000 psi | |
| Carpenter Custom 455® Stainless Steel, Annealed, 25 mm Bar Data provided by Carpenter Technology Corporation.Recognizing the need for high-strength alloys with good corrosion resistance to atmospheric environments, the Carpenter Research Laboratory develope.. |
|||