- Latrobe Lescalloy® 17-4 VAC-ARC Precipitation Hardening Stainless Steel
Latrobe Lescalloy® 17-4 VAC-ARC Precipitation Hardening Stainless Steel
| Category | Metal , Ferrous Metal , Martensitic , Stainless Steel , Precipitation Hardening Stainless |
| Manufacturer | Latrobe Steel |
| Trade Name | Lescalloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Latrobe Lescalloy® 17-4 VAC-ARC Precipitation Hardening Stainless Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150°F (482-621°C) temperature range. Vacuum arc remelting provides low gas content, superior cleanliness and optimum transverse properties.H900 Condition - Information Provided by Timken Latrobe Steel.Timken sold Latrobe in December 2006. They are now Latrobe Specialty Steels Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.81 g/cc | 0.282 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | >= 931 MPa | >= 135000 psi | H1150 Condition - 620°C at 4 hr |
| >= 1000 MPa | >= 145000 psi | H1075 Condition - 580°C at 4 hr | |
| >= 1310 MPa | >= 190000 psi | H900 Condition - 480°C at 1 hr | |
| Tensile Strength, Yield | >= 724 MPa @Strain 0.200 % |
>= 105000 psi @Strain 0.200 % |
H1150 Condition - 620°C at 4 hr |
| >= 860 MPa @Strain 0.200 % |
>= 125000 psi @Strain 0.200 % |
H1075 Condition - 580°C at 4 hr | |
| >= 1170 MPa @Strain 0.200 % |
>= 170000 psi @Strain 0.200 % |
H900 Condition - 480°C at 1 hr | |
| Elongation at Break | >= 10 % | >= 10 % | H900 Condition - 480°C at 1 hr |
| >= 13 % | >= 13 % | H1075 Condition - 580°C at 4 hr | |
| >= 16 % | >= 16 % | H1150 Condition - 620°C at 4 hr | |
| Reduction of Area | >= 35 % | >= 35 % | H900 Condition - 480°C at 1 hr |
| >= 45 % | >= 45 % | H1075 Condition - 580°C at 4 hr | |
| >= 50 % | >= 50 % | H1150 Condition - 620°C at 4 hr | |
| Modulus of Elasticity | 197 GPa | 28500 ksi | Tension |
| Poissons Ratio | 0.272 | 0.272 | |
| Shear Modulus | 77.2 GPa | 11200 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.0 µm/m-°C @Temperature 21.0 - 204 °C |
6.11 µin/in-°F @Temperature 69.8 - 399 °F |
|
| 11.7 µm/m-°C @Temperature 21.0 - 427 °C |
6.50 µin/in-°F @Temperature 69.8 - 801 °F |
||
| Specific Heat Capacity | 0.460 J/g-°C @Temperature 0.000 - 100 °C |
0.110 BTU/lb-°F @Temperature 32.0 - 212 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.040 % | 0.040 % | |
| Chromium, Cr | 15.7 % | 15.7 % | |
| Copper, Cu | 3.5 % | 3.5 % | |
| Iron, Fe | 74.6 % | 74.6 % | |
| Manganese, Mn | 0.65 % | 0.65 % | |
| Nb + Ta | 0.30 % | 0.30 % | |
| Nickel, Ni | 4.7 % | 4.7 % | |
| Silicon, Si | 0.35 % | 0.35 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000769 ohm-cm | 0.0000769 ohm-cm |
Users viewing this material also viewed the following:
- Parabeam Industrie Paraglass 5 3D Glass Fabric
- Advanced Elastomer Systems VistaFlex® 911-N Thermoplastic Rubber (discontinued **)
- Momentive Performance Materials IS808 One-Component, Paste Consistency Silicone Rubber Adhesive Sealant, Translucent
- Solvay Specialty Polymers FOMBLIN® M60 PFPE Lubricant
- Saint-Gobain CHR® 2829-5(R) Acrylic Adhesive Zone Tape
- Solvay RHODAFAC® AAP Surfactant
- Chase Plastics CP Pryme® N140MGHSL (COND, 50% RH) Nylon 6, 40% Mineral/Glass Reinforced, Heat Stabilized, Internally Lubricated
- A. Schulman LP554-01 Narrow Molecular Weight Homopolymer, High-Density Polyethylene
- Arlon 41600R025 0.025" Uncured, Unsupported Silicone Rubber on Release Carrier
Copyright © lookpolymers.com All Rights Reserved