TIMET TIMETAL® 62S Titanium Alloy (Ti-6Al-2Fe-0.1Si); Annealed Sheet/Plate & Billet/Bar

Category	Metal , Nonferrous Metal , Titanium Alloy , Beta Titanium Alloy
Manufacturer	TIMET
Trade Name	TIMETAL®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	TIMET TIMETAL® 62S Titanium Alloy (Ti-6Al-2Fe-0.1Si); Annealed Sheet/Plate & Billet/Bar.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Low Cost, Multipurpose Alloy. Tensile property data below for Annealed Sheet/Plate & Billet/Bar.Features: Properties and processing characteristics equivalent to or better than TIMETAL 6-4, but with significantly higher stiffness (elastic modulus). Due to the use of iron as the beta stabilizer, the alloy has lower formulation costs than TIMETAL 6-4. The combination of reasonable cost and excellent mechanical properties make TIMETAL 62S a practical substitute for many engineering materials.Typical heat treatment for this alloy: Mill Anneal at 760°C for 1-2 hrs, air cool Data provided by TIMET.

Physical Properties	Metric	English	Comments
Density	4.44 g/cc	0.160 lb/in³	Typical

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1000 MPa	145000 psi	Typical
Tensile Strength, Yield	960 MPa @Strain 0.200 %	139000 psi @Strain 0.200 %	Typical
Elongation at Break	16 %	16 %	Typical
Modulus of Elasticity	128 GPa	18600 ksi	Typical
Fatigue Strength	600 MPa	87000 psi	Limit; test specifics not reported
Bend Radius, Minimum	4.5 t	4.5 t	Typical; on 0.078 in (2 mm) sheet

Thermal Properties	Metric	English
CTE, linear	8.60 µm/m-°C @Temperature 20.0 °C	4.78 µin/in-°F @Temperature 68.0 °F
	9.70 µm/m-°C @Temperature 250 °C	5.39 µin/in-°F @Temperature 482 °F
	10.6 µm/m-°C @Temperature 500 °C	5.89 µin/in-°F @Temperature 932 °F
Specific Heat Capacity	0.500 J/g-°C	0.120 BTU/lb-°F
Thermal Conductivity	8.60 W/m-K	59.7 BTU-in/hr-ft²-°F
Beta Transus	1024 °C	1875 °F

Component Elements Properties	Metric	English	Comments
Aluminum, Al	5.5 - 6.5 %	5.5 - 6.5 %
Carbon, C	<= 0.080 %	<= 0.080 %
Hydrogen, H	<= 0.0125 %	<= 0.0125 %
Iron, Fe	1.3 - 2.0 %	1.3 - 2.0 %
Nitrogen, N	<= 0.040 %	<= 0.040 %
Oxygen, O	0.15 - 0.20 %	0.15 - 0.20 %
Silicon, Si	0.070 - 0.13 %	0.070 - 0.13 %
Titanium, Ti	90.7 - 93 %	90.7 - 93 %	Calculated as remainder

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.000163 ohm-cm	0.000163 ohm-cm