- Polymer Property : Tensile Strength, Ultimate = 110000 psi
Polymer Property : Tensile Strength, Ultimate = 110000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | >= 758 MPa | >= 110000 psi | |
| PSM Industries PolyAlloys WNF-2109 Tungsten Heavy Alloy Mil. T-21014 Class 4, SAE-AMS-T-21014 Class 4, ASTM-B-777-87 Class 4Information Provided by PolyAlloys, a division of PSM Industries |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | |
| Hogen HM1000 Tungsten-Based Metal Mil Spec T-21014D Class 1; ASTM B-777-99 Class 1; SAE Aero Material Spec (AMS) 7725C; AMS T-21014 Class 1. Nil magnetic properties.Manufactured by powder metallurgy methods. The tungsten base offe.. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | |
| Hogen HM3000 Tungsten-Based Metal Mil Spec T-21014D Class 3; ASTM B-777-99 Class 3; AMS T-21014 Class 3. Nil magnetic properties.Manufactured by powder metallurgy methods. The tungsten base offers high thermal conductivity and a l.. |
|||
| Tensile Strength, Ultimate | 759 MPa @Temperature 538 °C |
110000 psi @Temperature 1000 °F |
|
| Kennametal Stellite Stellite® 6 PM cast Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
| Tensile Strength, Ultimate | >= 760 MPa | >= 110000 psi | |
| MetalTek MTEK CA6NM Cast UNS J91540 Martensitic Stainless Steel "400" series, General corrosion resistant alloys, high strength.Applications: Chemical and food process equipment, jet engine compressor cases and rocket engine parts.Information provided by MetalTe.. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | |
| Mi-Tech Metals HD18 Tungsten-Based Metal Mil Spec T-21014D Class 3; ASTM B-777-99 Class 3; ASTM B-777-07 Class 3; AMS T-21014 Class 3. Nil magnetic properties.Manufactured by powder metallurgy methods. The tungsten base offers high therm.. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | 4140 Steel butt joint |
| Lucas-Milhaupt EASY FLO Silver Based Cadmium-Bearing Filler Metal Applications: Easy-Flo is very versatile and can be used successfully on nearly all nickel, iron and copper base alloys. In certain instances, special fluxes, may be required to obtain good wettin.. |
|||
| Tensile Strength, Ultimate | 758 - 1034 MPa | 110000 - 150000 psi | |
| Materion Beryllium Nickel Strip - Alloy 360 1/4 Hard Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: as suppliedFormability Ratio, 90° Bend, Radius/Thickness (Good Way): 0Formability Ratio (bad Way): .. |
|||
| Tensile Strength, Ultimate | 760 MPa @Temperature 205 °C |
110000 psi @Temperature 401 °F |
|
| Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Tensile Strength, Ultimate | 760 MPa | 110000 psi | Annealed prior to test |
| Special Metals BRIGHTRAY® Alloy C Electrical Resistance Alloy A nickel-chromium electrical-resistance alloy for use at operating temperatures up to 2100°F (1150°C). It contains rare-earth additions for increased oxidation resistance, especially under co.. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | |
| Special Metals INCONEL® 690 Nickel Superalloy, Cold Drawn Tube, 0.50 inch (12.7 mm) o.d. and 0.050 inch (1.27 mm) Thickness Composition adjustments for nuclear applications: 28-31 Cr; 0.04 max C; 0.10 max Co.Tensile strength (ultimate and yield) and elongation values reported here are typical for Cold Drawn Tube, 0.50 in.. |
|||
| Tensile Strength, Ultimate | 760 MPa @Temperature 650 °C |
110000 psi @Temperature 1200 °F |
Annealed prior to test |
| Special Metals INCONEL® Alloy 625 Niobium content includes tantalum. A nickel-chromium-molybdenum alloy with an addition of niobium that acts with the molybdenum to stiffen the alloy's matrix and thereby provide high strength witho.. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | Typical Annealed |
| Special Metals INCONEL® C276 Nickel Superalloy Bar Tensile strength (ultimate and yield) and elongation values reported here are typical for annealed bar. Other property values are typical of INCO® C276.Data provided by the manufacturer, Special .. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | |
| Universal Wire Works 625 Nickel Alloy Welding Wire Alloy 625 is used for TIG, MIG and submerged-arc welding of Inconel type alloys 601 and 625, Incoloy type alloy 800, as well as overlaying on steel and joining 9% nickel steel. Alloy 625 can be used.. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | Drawn rod and bar |
| CMW® 100 Copper Alloy CMW® 100 material is a heat treatable, high strength, high conductivity copper base alloy. Its properties are a combination of highest strength and hardness with relatively high electrical and ther.. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | Typical |
| Dura-Bar 100-70-03 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | cold worked |
| CMW® ELKONIUM 43 palladium based alloy Palladium belongs to the platinum group of metals and like platinum is highly resistant to atmospheric corrosion; however, it begins to tarnish at temperatures above 400(C. It has a high melting poi.. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | Annealed |
| AK Steel 201LN Austenitic Stainless steel AK Steel 210 was developed originally to conserve nickel. It provides properties similar to Type 301 and can be used in most applications for Type 301. This alloy is non-magnetic in the annealed c.. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | Annealed |
| AK Steel 301 Austenitic Stainless steel AK Steel 301 provides high strength and good ductility when cold worked. It is a modification of AK Steel 302 to increase the cold work-hardening range, to permit higher tensile strengths to be ach.. |
|||
| Tensile Strength, Ultimate | 760 MPa | 110000 psi | |
| ATI Allegheny Ludlum Grade 18 Titanium (UNS R56322) Uses: heat exchangers, industrial components, tubing.Mechanical property data below is typical of annealed samples at room temperature.Information provided by Allegheny Ludlum. |
|||
| Tensile Strength, Ultimate | 759 MPa | 110000 psi | |
| ATI Allvac® Nickelvac® 606 Nickel Superalloy Uses: Weld wire, woven wire mesh belts.Property values are for samples in the metallurgical condition: 2000°F anneal + water quench.Information provided by Allvac, An Allegheny Teledyne Company. |
|||
| Tensile Strength, Ultimate | 759 MPa | 110000 psi | |
| ATI Allvac® Nickelvac® XM-19 UNS S20910 Specialty Steel Uses: Chemical processing equipment, high-strength pump shafts, surgical implants, intermedullary nails, plates, screws, wires.Property values are for samples in the metallurgical condition: 1900°F.. |
|||
| Tensile Strength, Ultimate | >= 760 MPa | >= 110000 psi | |
| Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; A (A) Temper; All Sizes (UNS N03360) Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011. |
|||
| Tensile Strength, Ultimate | >= 758 MPa | >= 110000 psi | |
| Materion ToughMet® T3 AT90 (OD ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have engin.. |
|||
| Tensile Strength, Ultimate | >= 758 MPa | >= 110000 psi | |
| Materion ToughMet® T3 CX105 (OD ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have engin.. |
|||
| Tensile Strength, Ultimate | 760 MPa | 110000 psi | |
| ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 50% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | |
| Haynes Hastelloy® C-22® alloy, SMAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||