- Special Metals INCONEL® 690 Nickel Superalloy, Cold Drawn Tube, 0.50 inch (12.7 mm) o.d. and 0.050 inch (1.27 mm) Thickness
Special Metals INCONEL® 690 Nickel Superalloy, Cold Drawn Tube, 0.50 inch (12.7 mm) o.d. and 0.050 inch (1.27 mm) Thickness
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® 690 Nickel Superalloy, Cold Drawn Tube, 0.50 inch (12.7 mm) o.d. and 0.050 inch (1.27 mm) Thickness.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Composition adjustments for nuclear applications: 28-31 Cr; 0.04 max C; 0.10 max Co.Tensile strength (ultimate and yield) and elongation values reported here are typical for Cold Drawn Tube, 0.50 inch (12.7 mm) o.d. and 0.050 inch (1.27 mm) Thickness. Other property values are typical of INCONEL® alloy 690.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.19 g/cc | 0.296 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | |
| Tensile Strength, Yield | 461 MPa @Strain 0.200 % |
66800 psi @Strain 0.200 % |
|
| Elongation at Break | 39 % | 39 % | |
| Modulus of Elasticity | 211 GPa | 30600 ksi | |
| Poissons Ratio | 0.289 | 0.289 | |
| Shear Modulus | 81.8 GPa | 11900 ksi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.06 µm/m-°C @Temperature 24.0 - 100 °C |
7.811 µin/in-°F @Temperature 75.2 - 212 °F |
Mean |
| 14.53 µm/m-°C @Temperature 24.0 - 300 °C |
8.072 µin/in-°F @Temperature 75.2 - 572 °F |
Mean | |
| 15.19 µm/m-°C @Temperature 24.0 - 500 °C |
8.439 µin/in-°F @Temperature 75.2 - 932 °F |
Mean | |
| 17.41 µm/m-°C @Temperature 20.0 - 1000 °C |
9.672 µin/in-°F @Temperature 68.0 - 1830 °F |
Mean, extrapolated | |
| Specific Heat Capacity | 0.450 J/g-°C | 0.108 BTU/lb-°F | |
| Thermal Conductivity | 13.5 W/m-K | 93.7 BTU-in/hr-ft²-°F | |
| Melting Point | 1343 - 1377 °C | 2449 - 2511 °F | |
| Solidus | 1343 °C | 2449 °F | |
| Liquidus | 1377 °C | 2511 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.050 % | <= 0.050 % | |
| Chromium, Cr | 27 - 31 % | 27 - 31 % | |
| Copper, Cu | 0.50 % | 0.50 % | |
| Iron, Fe | 7.0 - 11 % | 7.0 - 11 % | |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Nickel, Ni | >= 58 % | >= 58 % | |
| Silicon, Si | <= 0.50 % | <= 0.50 % | |
| Sulfur, S | <= 0.15 % | <= 0.15 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0001148 ohm-cm | 0.0001148 ohm-cm | |
| Magnetic Permeability | 1.001 | 1.001 | at 200 Oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-BOND 1069, Part A Silicone Rubber Mixture
- Momentive Performance Materials Siloprenâ„¢ FFSL 7061 Fully Fluorinated Liquid Silicone Rubber
- Borealis BorPEX™ HE2556 Black High Density Polyethylene Powder for Crosslinked Pipes
- Wieland 1945 Wilaform Platinum
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 40 PHR N330 (HAF) Black
- Chevron Phillips Marlex® 1007 Injection Molding Resin
- Diamond Polymers ASA T-115
- Aclo Accutech Polypropylene Homopolymer HP0336M20L Mica Reinforced
- BASF Neopolen® P 8220 K 0.03 g/cc Core density; Expanded Polypropylene (Europe)
- Ashley Polymers Ashlene® 528LS-33GB Nylon 66, Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved