Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 40.0 - 180 MPa | 5800 - 26100 psi | Average value: 146 MPa Grade Count:26 |
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45.. |
|||
Tensile Strength, Ultimate | 2.70 - 180 MPa | 392 - 26100 psi | Average value: 77.9 MPa Grade Count:49 |
Overview of materials for Polyetheretherketone, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PTFE Filled". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Ultimate | 70.0 - 180 MPa @Temperature 125 - 275 °C |
10200 - 26100 psi @Temperature 257 - 527 °F |
Average value: 123 MPa Grade Count:1 |
Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Carbon Fiber Filled". Each property range of values reported .. |
|||
Tensile Strength, Ultimate | 34.5 - 180 MPa | 5000 - 26100 psi | Average value: 93.7 MPa Grade Count:36 |
Overview of materials for Polyphenylene Sulfide (PPS) with 10% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 10% Glass Fiber Filler". Specific grades with glass content between 5% .. |
|||
Tensile Strength, Ultimate | 115 - 180 MPa @Temperature 70.0 - 175 °C |
16700 - 26100 psi @Temperature 158 - 347 °F |
Average value: 139 MPa Grade Count:4 |
Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E.. |
|||
Tensile Strength, Ultimate | 115 - 180 MPa @Time 180000 - 7.20e+7 sec |
16700 - 26100 psi @Time 50.0 - 20000 hour |
Average value: 139 MPa Grade Count:4 |
Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E.. |
|||
Tensile Strength, Ultimate | 25.9 - 180 MPa | 3760 - 26100 psi | Average value: 114 MPa Grade Count:183 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Tensile Strength, Ultimate | 13.8 - 180 MPa | 2000 - 26100 psi | Average value: 105 MPa Grade Count:277 |
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea.. |
|||
Tensile Strength, Ultimate | 59.2949 - 180 MPa @Temperature -40.0 - 204 °C |
8600.01 - 26100 psi @Temperature -40.0 - 400 °F |
Average value: 115 MPa Grade Count:5 |
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS)- 40% Glass filled; Molded". Specific grades with glass content between 35% a.. |
|||
Tensile Strength, Ultimate | 41.1 - 180 MPa | 5960 - 26100 psi | Average value: 111 MPa Grade Count:52 |
Overview of materials for Polytrimethylene Terephthalate (PTT) This property data is a summary of similar materials in the MatWeb database for the category "Polytrimethylene Terephthalate (PTT)". Each property range of values reported is minimum and maximum val.. |