Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 20.0 - 140 MPa | 2900 - 20300 psi | Average value: 99.8 MPa Grade Count:210 |
Overview of materials for Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled". Specific grades with glass content between 15.. |
|||
Tensile Strength, Ultimate | 65.0 - 140 MPa | 9430 - 20300 psi | Average value: 105 MPa Grade Count:5 |
Overview of materials for Polyethylene Terephthalate (PET), Recycled, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Recycled, Glass/Mineral Reinforced". Each property range of values rep.. |
|||
Tensile Strength, Ultimate | 36.0 - 140 MPa | 5220 - 20300 psi | Average value: 80.4 MPa Grade Count:7 |
Overview of materials for Nylon 6, Mineral Reinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Mineral Reinforced, Impact Grade". Each property range of values reported is minimum and maximu.. |
|||
Tensile Strength, Ultimate | 40.0 - 140 MPa @Temperature 60.0 - 150 °C |
5800 - 20300 psi @Temperature 140 - 302 °F |
Average value: 78.1 MPa Grade Count:5 |
Overview of materials for Nylon 66, Heat Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Heat Stabilized". Each property range of values reported is minimum and maximum values of appr.. |
|||
Tensile Strength, Ultimate | 90.0 - 140 MPa @Temperature 60.0 - 150 °C |
13100 - 20300 psi @Temperature 140 - 302 °F |
Average value: 113 MPa Grade Count:1 |
Overview of materials for Nylon 66, 20% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Carbon Fiber Filled". Specific grades with carbon fiber content between 15% and 24% are in.. |
|||
Tensile Strength, Ultimate | 60.0 - 140 MPa @Temperature 60.0 - 150 °C |
8700 - 20300 psi @Temperature 140 - 302 °F |
Average value: 95.6 MPa Grade Count:2 |
Overview of materials for Nylon 612, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Glass Fiber Filler". Each property range of values reported is minimum and maximum values of .. |
|||
Tensile Strength, Ultimate | 60.0 - 140 MPa | 8700 - 20300 psi | Average value: 110 MPa Grade Count:30 |
Overview of materials for Nylon 12, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 50.0 - 140 MPa | 7250 - 20300 psi | Average value: 72.5 MPa Grade Count:4 |
Overview of materials for Nylon, Amorphous Transparent Alloy This property data is a summary of similar materials in the MatWeb database for the category "Nylon, Amorphous Transparent Alloy". Each property range of values reported is minimum and maximum value.. |
|||
Tensile Strength, Ultimate | 110 - 140 MPa | 16000 - 20300 psi | ASTM D638 |
Chang Chun Plastic PBT3030 30% Glass Fiber Enforced PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 110 - 140 MPa | 16000 - 20300 psi | ASTM D638 |
Chang Chun Plastic PBT4830 Fire Retardant & 30% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 110 - 140 MPa | 16000 - 20300 psi | ASTM D638 |
Chang Chun Plastic PBT4130 Fire Retardant & 30% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd. |