Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 5.52 - 6.21 MPa | 800 - 900 psi | |
Sika Industry SikaFlex 255FC Fast Cure One Part Polyurethane Adhesive Sika 255FC SikaFlex Fast Cure One Part Polyurethane AdhesiveThis is a fast curing flexible high performance polyurethane adhesive for bonding glass to metal surfaces. Initial strength is derived fro.. |
|||
Tensile Strength, Ultimate | 5.52 - 6.21 MPa | 800 - 900 psi | |
Sika Industry SikaTack UltraFast Fast Cure One Part Polyurethane Adhesive Sika UltraFast SikaTack Fast Cure One Part Polyurethane AdhesiveThis revolutionary product uses heat instead of moisture to "pre-cure" the adhesive. The product is heated before applications using a.. |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | |
Williams Advanced Alloys WS143 Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | |
Dow Corning HV 1551/70P 40 Shore hardness low viscosity injection mouldable liquid silicone rubber with high tear strength, high elongation and a fast cure speed.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | |
Dow Corning SILASTIC® E RTV SILICONE RUBBER KIT High strength silicone mold making rubber recommended for use with polyester or plaster and can be used with rigid and foam polyurethanes and epoxies.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 51106RB015D Silicone Rubber/Fiberglass Laminate Interleave 2: 3 mil PE; Side 2: cured silicone rubber; Substrate: 7628 fiberglass; Side 1: uncured silicone rubber, Interleave 1: 3 mil PE |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 51141R015 Silicone Rubber/Fiberglass Laminate Interleave 1: 3 mil PE; Side 1: uncured silicone rubber; Substrate: 7628 fiberglass; Side 2: uncured silicone rubber; Interleave 2: 3 mil PE |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 51146R020 Silicone Rubber/Fiberglass Laminate Side 1: cured silicone rubber; Substrate: 7628 fiberglass; Side 2: uncured silicone rubber; Interleave: 3 mil polyethylene |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 56276R026 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Side 2: uncured silicone rubber; Substrate: 162 fiberglass; Side 1: cured silicone rubber |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | ASTM D412 |
Arlon CP-510R Silicone Rubber bulk compound |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | After 7 days at 257°F (125°C); ASTM D573; ISO 188 |
Advanced Polymer Alloys Alcryn® 2070 NC Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod.. |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 51106R020 Silicone Rubber/Fiberglass Laminate Side 1: cured silicone rubber; Substrate: 7628 fiberglass; Side 2: uncured silicone rubber; Interleave: 3 mil polyethylene |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 51141R020 Silicone Rubber/Fiberglass Laminate Interleave 1: 3 mil PE; Side 1: uncured silicone rubber; Substrate: 7628 fiberglass; Side 2: uncured silicone rubber; Interleave 2: 3 mil PE |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 51146R015 Silicone Rubber/Fiberglass Laminate Side 1: cured silicone rubber; Substrate: 7628 fiberglass; Side 2: uncured silicone rubber; Interleave: 3 mil polyethylene |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 51276R020 Silicone Rubber/Fiberglass Laminate Side 1: cured silicone rubber; Substrate: 7628 fiberglass; Side 2: uncured silicone rubber; Interleave: 3 mil polyethylene |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 55106R028 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Side 2: uncured silicone rubber; Substrate: 162 fiberglass; Side 1: cured silicone rubber |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property, layer 1; ASTM D412 |
Arlon 55109R028 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Layer 2: uncured silicone rubber; Layer 1: cured silicone rubber; Substrate: 162 fiberglass |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property, side 1; ASTM D412 |
Arlon 55141R028 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Side 1: uncured silicone rubber; Substrate: 162 fiberglass; Side 2: uncured silicone rubber; Interleave 2: 3 mil PE |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property, side 2; ASTM D412 |
Arlon 55141R028 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Side 1: uncured silicone rubber; Substrate: 162 fiberglass; Side 2: uncured silicone rubber; Interleave 2: 3 mil PE |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 55143R060 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Side 2: cured silicone rubber; Substrate: 162 fiberglass; Side 1: cured silicone rubber |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 55146R028 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Side 2: uncured silicone rubber; Substrate: 162 fiberglass; Side 1: cured silicone rubber |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 55149R062 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Layer 2: uncured silicone rubber; Layer 1: cured silicone rubber; Substrate: 162 fiberglass |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | ASTM D412 |
Arlon CP-427R Silicone Rubber bulk compound |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | |
BCC Products BC 9060 Silicone RTV Rubber BC 9060 is a blue colored, two-component, flowable compound that, regardless of thickness or confinement, cures at room temperature or by application heat. The cured rubber is high strength and high.. |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | After 7 days at 257°F (125°C); ASTM D573; ISO 188 |
Advanced Polymer Alloys Alcryn® 2080 NC Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod.. |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | ASTM D638 |
Colorite Polymers 4875 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 55279R028 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Layer 2: uncured silicone rubber; Layer 1: cured silicone rubber; Substrate: 162 fiberglass |
|||
Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
Arlon 55276R028 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Side 2: uncured silicone rubber; Substrate: 162 fiberglass; Side 1: cured silicone rubber |