Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | ASTM Data |
Americas Styrenics Styron® 6010 High Impact Polystyrene
(discontinued **) STYRON® 6010 resin is a high impact polystyrene grade with a proprietary ignition resistance additive package to achieve a UL 94 V-0 rating. It offers high heat resistance, high modulus, good impac.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | |
Ineos Styrenics Polystyrene 476M Q598 (NAFTA) High-impact grade of polystyrene with good ESCR designed to provide uniform melt flow for excellent processability.Information provided by BASF.Ineos Styrenics purchased this product line from BASF .. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | 50mm/min; ASTM D638 |
Micropol Microlink XL28/FR Black Crosslinkable Polyethylene Flame retardant. Provides a finished molding of improved properties with the use of conventional rotational molding equipment. Properties include enhanced toughness (particularly low temp impact),.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | ASTM D638 |
LyondellBasell Astryn 65F4-4 Polypropylene Homopolymer, 40% Talc Key Features: conventional melt flow, high modulus, mineral-filled polypropylene homopolymer, high stiffness, good dimensional stability, excellent heat resistanceApplications: automotive heater and.. |
|||
Tensile Strength, Ultimate | 23.0 MPa @Temperature 1260 °C |
3340 psi @Temperature 2300 °F |
|
Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Tensile Strength, Ultimate | 23.0 MPa @Temperature 22.0 °C |
3340 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® BMC 3000 Unsaturated Polyester UP BMC 3000 is a special BMC suitable for the use in microwave and cookware applications.It has high temperature resistance, and meets requirements for food contact applications. It has a high gloss fi.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | 35'/145°C; ASTM D412 |
SYNTHOS Kralex® 1500 Styrene Butadiene Rubber KRALEX® 1500 is a standard grade of styrene butadiene rubber. It is produced by a technology of cold emulsion polymerization based on soaps of rosin acids and contains 23.5% of chemically bonded .. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | 35'/145°C; ASTM D412 |
SYNTHOS Kralex® 1501 Styrene Butadiene Rubber KRALEX® 1501 is a standard grade of styrene butadiene rubber. It is produced by a technology of cold emulsion polymerization based on soaps of rosin acids and contains 23.5% of chemically bonded .. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | 35'/145°C; ASTM D412 |
SYNTHOS Kralex® 1507 Styrene Butadiene Rubber KRALEX® 1507 is a standard grade of styrene butadiene rubber. It is produced by a technology of cold emulsion polymerization based on soaps of rosin and fatty acids and contains 23.5% of chemical.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 670 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 555-31 Recycled Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 555-31 Recycled Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | ASTM D638/D412 |
Covestro Bayflex® 110-50 CM Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and o.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | ASTM D638/D412 |
Covestro Bayflex® 110-50 Polyurethane Elastomeric RIM, 15% Mineral Filled, MDI-based 2-Component Liquid System Mineral filler is RRIMGLOS® 10013. 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialSc.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | Die C (35 min / 145°C); ASTM D412 |
Dow Buna® SB 1712 Cold polymerized Emulsion Styrene Butadiene Rubber (E-SBR) Buna® SB 1712 - Schkopau is manufactured by cold polymerization using mixed rosin acid / fatty acid soaps. It is plasticized with 37.5 parts of an aromatic oil in relation to solid rubber. A disc.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | Die C (35 min / 145°C); ASTM D412 |
Dow Buna® SB 1723 Cold polymerized Emulsion Styrene Butadiene Rubber (E-SBR) Buna® SB 1723 - Schkopau is manufactured by cold polymerization using mixed rosin acid / fatty acid soaps. It is plasticized with 37.5 parts of a TDAE oil in relation to solid rubber. A discolori.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | Die C (35 min / 145°C); ASTM D412 |
Dow SE SLR-6410 Solution polymerized Styrene Butadiene Rubber (S-SBR) SE SLR-6410 is manufactured by anionic solution polymerization using lithium initiator and is extended with 50 parts of aromatic oil in relation to solid rubber. It is a product with medium styrene.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | typical Tyrin resin w/ Ba-Cd stabilizer, Epoxidized soybean oil, phosphite chelator, and lubricant. |
Dow Tyrin® 3615P Chlorinated Polyethylene Elastomer 36% Chlorine. Tyrin® chlorinated polyethylene thermoplastic resins offer the compounding and fabrication industries end product properties in a range of hardnesses, and behave much like flexible P.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | typical Tyrin resin w/ Ba-Cd stabilizer, Epoxidized soybean oil, phosphite chelator, and lubricant. |
Dow Tyrin® 3611P Chlorinated Polyethylene Elastomer 36% Chlorine. Tyrin® chlorinated polyethylene thermoplastic resins offer the compounding and fabrication industries end product properties in a range of hardnesses, and behave much like flexible P.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | typical Tyrin resin w/ Ba-Cd stabilizer, Epoxidized soybean oil, phosphite chelator, and lubricant. |
Dow Tyrin® 3623A Chlorinated Polyethylene Elastomer 36% Chlorine. Tyrin® chlorinated polyethylene thermoplastic resins offer the compounding and fabrication industries end product properties in a range of hardnesses, and behave much like flexible P.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | ASTM D638 |
A. Schulman ComAlloy Voloy® 101 Polypropylene, Impact Modified, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | ASTM D638 |
Solvay Specialty Polymers Algoflon® E2 PTFE (Polytetrafluoroethylene)
(discontinued **) Data provided by the manufacturer.Pre Sintered. Type V Classification. Suspension polymer powder grade recommended for compression molding and extrusion. PTFE possesses high inertness, excellent di.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | ASTM D638 |
Solvay Specialty Polymers Algoflon® E2 BP PTFE (Polytetrafluoroethylene)
(discontinued **) Data provided by the manufacturer.Pre Sintered. Type V Classification. Suspension polymer powder grade recommended for compression molding and extrusion. PTFE possesses high inertness, excellent di.. |
|||
Tensile Strength, Ultimate | 23.0 - 52.0 MPa @Temperature 260 - 260 °C |
3340 - 7540 psi @Temperature 500 - 500 °F |
Average value: 33.3 MPa Grade Count:4 |
Overview of materials for Polyimide, Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyimide, Graphite Filled". Each property range of values reported is minimum and maximum values of app.. |
|||
Tensile Strength, Ultimate | 23.0 - 42.7 MPa | 3340 - 6190 psi | Average value: 33.6 MPa Grade Count:67 |
Overview of materials for Cellulose Acetate Propionate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Propionate, Molded". Each property range of values reported is minimum and maximum val.. |
|||
Tensile Strength, Ultimate | 23.0 - 80.0 MPa @Temperature 160 - 160 °C |
3340 - 11600 psi @Temperature 320 - 320 °F |
Average value: 68.8 MPa Grade Count:2 |
Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | ASTM D638 |
ExxonMobil Iotek® 7030 Zinc Ionomer Molding/Extrusion Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A zinc ionomer with excellent flexibility, abrasion resistance, impact strength and tensile strength. This ionomer has outstanding adhesion to glas.. |
|||
Tensile Strength, Ultimate | 23.0 MPa @Temperature -20.0 °C |
3340 psi @Temperature -4.00 °F |
Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 |
DuPont Elvax® 250 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |