- LyondellBasell Astryn 65F4-4 Polypropylene Homopolymer, 40% Talc
LyondellBasell Astryn 65F4-4 Polypropylene Homopolymer, 40% Talc
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | LyondellBasell |
| Trade Name | Astryn |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Astryn 65F4-4 Polypropylene Homopolymer, 40% Talc.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features: conventional melt flow, high modulus, mineral-filled polypropylene homopolymer, high stiffness, good dimensional stability, excellent heat resistanceApplications: automotive heater and A/C housings, small and large appliances, fan shrouds, housewares, utility productsDescription: Astryn 65F4-4 conventional melt flow, 40% talc-filled polypropylene homopolymer is designed for maximum stiffness, good dimensional stability and excellent heat aging performance.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792B |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | ASTM D638 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Modulus | 2.90 GPa | 421 ksi | Tangent at 0.05 in/min; ASTM D790A |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
Users viewing this material also viewed the following:
- LNP Thermocomp® STN-F-1006 HS Polyamide 46, Glass Fiber Reinforcement (discontinued **)
- Karina CAK 65-48/1 Black PVC Compound
- Williams Advanced Alloys WS232 Solder
- A. Schulman POLYBATCH™ Poly Off-White P90062PF Concentrate Based In Polypropylene
- Eastman Tritan WX500 Copolyester
- ExxonMobil Jayflex™ DIDP Plasticizer
- Chosun Refractories MCC-1 Magnesia Calcia Carbon Brick For Refining Ladle
- AK Steel ASTM A 607 Class 1 Formable, Grade 60K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA)
- BASF Lupranate® 5020 Isocyanate
- Overview of materials for Polyether Ester Elastomer
Copyright © lookpolymers.com All Rights Reserved