Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 185 MPa | 26900 psi | ASTM D638 |
Nylene® 5143 MS , 43% Glass Reinforced Low Wear Nylon 6/6 Description: Nylene® 5143 MS is a 43% glass fiber reinforced, low wear nylon 6/6. MoS2 - 2%. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies .. |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | Same value from ASTM and ISO tests; 5 mm/min. |
BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9233G is a 33% glass reinforced polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface aesthetics. It is.. |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | Same value from ASTM and ISO tests; 5 mm/min. |
BASF Capron® SEG7 35% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron SEG7 is an unfilled injection molding type 6 nylon graft copolymer. It has superior impact resistance and flow especially for thinner walled parts and long flow lengths. Copolymerization res.. |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | ASTM D638 |
Solvay Specialty Polymers Ixef® 1501/0003 Polyarylamide, 30% Glass Fiber, DAM
(discontinued **) The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay A.. |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | |
Indium Corp. Indalloy® 183 Au-Ge Solder Alloy Eutectic die attach.Information provided by the manufacturer, Indium Corporation. |
|||
Tensile Strength, Ultimate | 185 MPa | 26900 psi | |
Williams Advanced Alloys WS361 Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | ASMT D638 |
Toyobo TS401 PPS, 40% Glass Fiber Reinforced Key Feature: General Purpose Grade - balanced characteristics suitable for a broad range of uses.High performance injection-molding resin created from crystalline polyphenylene sulfide, using a spec.. |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1015G33-8 NAT PA6-GF33 33% Glass Reinforced, Injection Molding |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | dry; ISO 527-1/-2 |
DSM Stanyl® TS241B3 PA46-CF15 15% Carbon Reinforced, Lubricated |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | dry; ISO 527-1/-2 |
DSM Stanyl® TW241B3 PA46-CF15 15% Carbon Reinforced, Heat Stabilized, Lubricated |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | dry; ISO 527-1/-2 |
DSM Stanyl® TW271B3 (PA46+PTFE)-CF15 15% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | ISO 527-1/-2 |
DSM Arnite® AV2 370 XL PET-GF35 35% Glass Reinforced, Low Outgassing |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | ISO 527-1/-2 |
DSM Arnite® AV2 370 XT PET-GF35 35% Glass Reinforced, Applications with extremely narrow tolerances |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry) Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also.. |
|||
Tensile Strength, Ultimate | 185 MPa @Temperature 250 °C |
26800 psi @Temperature 482 °F |
Typical, after 10,000 hours |
Aleris Weldural Aluminum Alloy, 100 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | 5mm/min; ISO 527 |
BASF Ultramid® SEG7 35% Glass Filled PA6 (Dry) Ultramid SEG7 is a 35% glass reinforced, injection molding type 6 nylon requiring high strength, surface aesthetics, and good processability. This product has excellent surface appearance
while mai.. |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | dry; ISO 527-1/-2 |
DSM Stanyl® TS200B3 PA46-CF15 15% Carbon Reinforced |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | ISO 527 |
Solvay Specialty Polymers Ryton® R-4-220NA Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4-220NA is an advanced 40% fiberglass reinforced polyphenylene sulfide compound formulated for enhanced hydrolytic stability in applications re.. |
|||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | ISO 527 |
LATI LARTON K/30 30% Carbon Fiber Reinforced Polyphenylene sulfide (PPS)
(Unverified Data**) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |