Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 140 MPa | 20300 psi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Polyester (PET), 30 wt.% glass Thermoplastic Polyesters are resistant to most organic solvents, weak acids and alkalis. They are not recommended with strong acids and alkalis or for prolonged use in hot water. Data provided by t.. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | ISO 527 |
Solvay Specialty Polymers Primef® 5084 30% GF PPS, Lubricated Grade
(discontinued **) Contains PTFE lubricant. Used for injection molding of high performance parts. |
|||
Tensile Strength, Ultimate | 140 - 265 MPa @Temperature 60.0 - 150 °C |
20300 - 38400 psi @Temperature 140 - 302 °F |
Average value: 210 MPa Grade Count:1 |
Overview of materials for Polyphthalamide (PPA), Carbon Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Carbon Fiber". Each property range of values reported is minimum and maximum values of .. |
|||
Tensile Strength, Ultimate | 140 - 150 MPa @Temperature 80.0 - 80.0 °C |
20300 - 21800 psi @Temperature 176 - 176 °F |
Average value: 128 MPa Grade Count:4 |
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl.. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | Same value from ASTM and ISO tests; 5 mm/min. |
BASF Capron® 8231G 14% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8231G is a 14% glass fiber reinforced polyamide 6 molding compound possessing a balance of engineering properties combined with excellent processability and surface aesthetics. It is also av.. |
|||
Tensile Strength, Ultimate | 140 MPa @Temperature 982 °C |
20300 psi @Temperature 1800 °F |
|
Haynes HR-160® alloy, hot rolled and solution annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | ISO 527-1, 2 |
Polyplastics Duranex® 3300 Polybutylene Terephthalate (PBT), Standard, 30% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | ISO 527-1, 2 |
Polyplastics Duranex® 3306 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 30% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1010GN8-30 NAT PA6-GF30 FR 30% Glass Reinforced, Flame Retardant, Halogen free |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | dry; ISO 527-1/-2 |
DSM Stanyl® SC50 PA46-GF30 FR 30% Glass Reinforced, Flame Retardant, Halogen free and free of red phosphorous |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | cond; ISO 527-1/-2 |
DSM Stanyl® TE200F8 PA46-GF40 40% Glass Reinforced, Heat Stabilized, for E&E applications |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | cond; ISO 527-1/-2 |
DSM Stanyl® TS250F8 PA46-GF40 FR 40% Glass Reinforced, Flame Retardant, Heat Stabilized |
|||
Tensile Strength, Ultimate | 140 MPa @Temperature 120 °C |
20300 psi @Temperature 248 °F |
ISO 527-1/-2 |
DSM Stanyl® TW271B6 (PA46+PTFE)-CF30 30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5 mm/min |
Arkema Group Orgalloy® RS 6630 Nylon 66 Alloy, 30% Glass Fiber (Conditioned) RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional propertie.. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | ISO R527 |
Arkema Group Orgalloy® RS 6630 Polyamide 6.6 Alloy 30% Glass Fiber reinforced Polyamide Alloy, Rigid grade, Nylon 6.6 basedMolding of Engineering PartsInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | ASTM D638 |
Adell HR-36 30% Glass Reinforced Heat Stabilized PBT |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5mm/min; ISO 527 |
BASF Ultradur B 2300 G6 HR BK15116 30% Glass Filled PBT Ultradur B 2300 G6 HR BK15116 is a hydrolysis resistant, pigmented black 30% fiberglass reinforced PBT, exhibiting superior flow characteristics. Designed for improved latch
strength in automotive.. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4300 G6 LS High Speed BK15045 30% Glass Filled PBT |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Dry) Ultramid 8231G HS is a heat stabilized, 14% glass fiber reinforced nylon 6 injection molding compound. It is also available in non-heat stabilized (Ultramid 8231) and/or pigmented versions. The gla.. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | ASTM D638 |
A. Schulman ComAlloy Comtuf® 464 Glass Reinforced, Impact Modified, PBT Alloy Data provided by the manufacturer, ComAlloy International Company.50% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4406 G6 Q717 30% Glass Filled PBT Ultradur B 4406 G6 Q717 is an UL V0 injection molding, PBT grade with 30% glass fiber reinforcement. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | ASTM data at 5 mm/min. |
BASF Capron® 8334G Impact Modified, 40% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron 8334G is a heat stabilized, 40% glass fiber reinforced polyamide 6 molding compound developed for applications requiring a high level of stiffness combined with excellent impact performance. .. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | ISO 527 |
LATI LARPEEK 50 G/20 20% Glass Reinforced Polyetheretherketone (PEEK)
(discontinued **) Larpeek polyetheretherketone (PEEK) is a high performance thermoplastic offering cost effective performance in difficult environments across all industries. PEEK is temperature resistant (up to 250°.. |
|||
Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8333G HI HS BK-102 33% Glass Filled PA6 (Dry) Ultramid 8333G HI HS BK-102 is a 33% glass reinforced, heat stabilized, impact modified, pigmented black, PA6 injection molding compound developed for applications requiring improved dry as molded t.. |