BASF Ultradur B 4406 G6 Q717 30% Glass Filled PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | BASF |
| Trade Name | Ultradur B |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultradur B 4406 G6 Q717 30% Glass Filled PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultradur B 4406 G6 Q717 is an UL V0 injection molding, PBT grade with 30% glass fiber reinforcement.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 98 cm³/g | 98 cm³/g | Viscosity number |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 275 °C |
22 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5mm/min; ISO 527 |
| Elongation at Break | 2.1 % | 2.1 % | 5mm/min; ISO 527 |
| Tensile Modulus | 11.5 GPa | 1670 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 220 MPa | 31900 psi | ISO Data |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | 10 K/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
IEC 60250 |
| 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR Mistron Vapor Filler
- Lord Adhesives Aeroglaze® 9744 Epoxy Primer/Tie-Coat
- Taiwan Sheen Soon Sheenthane® D6320E Thermoplastic Polyurethane Elastomer
- A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6
- Unitika A1030GFL PA6, 30% Glass Fiber Reinforced, Conditioned
- Plenco 4414 Phenolic, Granular, Injection Molded
- DSM Arnitel® EL740-H/A Injection Molding; Other Extrusion Grade Copolyester Elastomer (North America)
- ChevronTexaco LS Diesel 2
- ExxonMobil LDPE LD 302.56 Low Density Polyethylene Resin
Copyright © lookpolymers.com All Rights Reserved