Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 172 MPa | 24900 psi | DIN 53455; ASTM D790 |
Kolon SPESIN® KP2122G15VO G/F Reinforced & Retardant PBT Resin
(discontinued **) SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High hea.. |
|||
Flexural Yield Strength | 172 MPa @Thickness 3.20 mm |
24900 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP2151BF PA66+GF15%, Flame Retardant Feature: Injection Molding, PA66+GF15%, Halogen Free Flame RetardantApplication: ConnectorsCAS No. 32131-17-2, 25038-54-4, 65997-17-3, 88497-56-7, 1309-64-4 and 138265-88-0Information provided by LG.. |
|||
Flexural Yield Strength | 172 MPa @Thickness 3.20 mm |
24900 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID SG4389B PA66+GF/MF38% Feature: Injection Molding, PA66+GF/MF38%Application: Automotive (Fan & Shroud)CAS No. 32131-17-2, 25038-54-4, 65997-17-3 and 14807-96-6Information provided by LG Chemical |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | DIN 53455; ASTM D790 |
Kolon KOPEL® KP3755 Specialty TPE Resin KOPEL® is a thermoplastic polyester elastomer which is a new engineering rubber having combined properties of conventional rubber and thermoplastic. Its flexibility and elastic recovery are very.. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL SE1GFN3 PPE+PS PPE+PS blend. 30% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 listing. RTI 110/105/110. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL SE1GFN3 PPE+PS (Asia Pacific) GR 30%. 275F (135C) DTUL. UL94 V-1 rated. Halogen free flame retardant. For electrical construction market. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2212EPR PEI 20% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA lising. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2212EPR PEI (Asia Pacific) 20% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA lising. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE 50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. ECO Conforming. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Asia Pacific) 50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. ECO Conforming. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Europe-Africa-Middle East) 50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. RoHS compliant. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Valox® 830R PBT (Asia Pacific) 30% glass filled, release grade, polyester alloy.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP DX99077 PC (Europe-Africa-Middle East) LNP* Thermocomp* DX99077 is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Non-.. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | ASTM D790 |
Samyang Tribit® 1500GN30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant Characteristics:G/F reinforcedFlame retardantHeat and Impact resistantApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A.. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | ASTM D790 |
Sumitomo Bakelite Durez® 23570 Phenolic, Injection Grade Durez 23570 Black Phenolic is a glass and mineral filled two-stage, special purpose molding material. It is designed for high strength, good dimensional stability, and electrical properties even aft.. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | ASTM D790 |
Cheng Yu Plastic ML3425 PC, 25% Glass Fiber |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | ASTM D790 |
Cheng Yu Plastic T883GV2 Flame Retardant PBT, 20% Glass Fiber |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | ASTM D790 |
Cheng Yu Plastic T889G2 PBT, 20% Glass Fiber |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | ASTM D790 |
Chem Polymer Chemlon 113 G Nylon 66, 13% Glass Fiber Reinforced A 13% glass fiber reinforced nylon 66 offering improved creep resistance, stiffness, tensile strength and dimensional stability over unmodified nylon 66 materials.Data provided by the manufacturer, .. |
|||
Flexural Yield Strength | 172 MPa | 24900 psi | DIN 53455; ASTM D790 |
Kolon SPELLOY® KB133G30 PC + PBT Alloy Resin
(discontinued **) SPELLOY® is a new technology of thermoplastic Polymer alloys developed to provide unique combination of excellent mechanical properties.High impact resistance (at low temperature), good dimensional.. |